Borealis PP BE50-7032
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Borealis AG |
| Trademark: | Borealis PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MqWesS_Borealis-PP-BE50-7032.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| BE50-7032 is a high molecular weight, low melt flow rate polypropylene homopolymer characterised by high stiffness, high heat distortion temperature and high resistance to thermal ageing. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.905 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/5.0 kg | 0.60 | g/10 min | ISO 1133 |
| 230°C/2.16 kg | 0.30 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1650 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 36.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 10 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 2.0 | kJ/m² | ISO 179/1eA |
| 23°C | 7.0 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 95.0 | °C | ISO 306/B50 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 190 - 230 | °C | |
| Cylinder Zone 2 Temp. | 190 - 230 | °C | |
| Cylinder Zone 3 Temp. | 190 - 230 | °C | |
| Cylinder Zone 4 Temp. | 190 - 230 | °C | |
| Cylinder Zone 5 Temp. | 190 - 230 | °C | |
| Melt Temperature | 200 - 230 | °C | |
| Die Temperature | 200 - 230 | °C |
| Extrusion instructions |
|---|
| Head Temperature: 200 to 230°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 105CC TFE 15 Z | RTP Company | PP Homopolymer | RTP |
| CALSIN LC102 | Pooya Polymer Tehran | Polyolefin, Unspecified | CALSIN |
| KEBATER® PBT B512A | BARLOG plastics GmbH | PBT | KEBATER® |
| Sylvin 9963-65 Red 6211 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LEXAN™ PC1800R resin | SABIC Innovative Plastics | PC | LEXAN™ |