Borealis PP PS65T20
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Borealis AG |
| Trademark: | Borealis PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MqDLuD_Borealis-PP-PS65T20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PS65T20 is a 20% mineral filled polypropylene compound intended for injection and back injection moulding. This material has excellent balanced mechanical properties and high melt flow rate. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 23 | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.2 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 90.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Injection Molded) | 2600 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, Injection Molded) | 32.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, Injection Molded) | 4.5 | % | ISO 527-2/50 |
| Flexural Modulus 1(Injection Molded) | 2700 | MPa | ISO 178 |
| Flexural Stress (Injection Molded) | 46.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C, injection molding | 1.5 | kJ/m² | ISO 179/1eA |
| 23°C, injection molding | 2.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C, injection molding | 15 | kJ/m² | ISO 179/1eU |
| 23°C, injection molding | 35 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | ||
| -20°C, injection molding | 2.0 | kJ/m² | ISO 180/1A |
| 23°C, injection molding | 3.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -20°C, injection molding | 12 | kJ/m² | ISO 180/1U |
| 23°C, injection molding | 30 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 110 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 60.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 154 | °C | ISO 306/A50 |
| -- | 96.0 | °C | ISO 306/B50 |
| Melt Energy | 85.5 | kJ/kg | ISO 11357 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Atomization- 16 hrs (100°C) | 6.0E-4 | g | DIN 75201 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Hopper Temperature | 40.0 - 80.0 | °C | |
| Processing (Melt) Temp | 220 - 260 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Holding Pressure | 30.0 - 60.0 | MPa |
| Injection instructions |
|---|
| Back pressure: Low to mediumScrew speed: Low to mediumFlow front speed: 100 - 200 mm/s |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRANSMARE® 14CT40-0.001 | Transmare Compounding B.V. | PP Copolymer | TRANSMARE® |
| Escorene™ Ultra UL 7760 | ExxonMobil Chemical | EVA | Escorene™ Ultra |
| Karina PURPLE COLOR CONCENTRATE 52/ 10FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ STAT-KON™ PD000 compound | SABIC Innovative Plastics Europe | Nylon 6 | LNP™ STAT-KON™ |
| Lupoy® GP5106F | LG Chem Ltd. | PC+ABS | Lupoy® |