LNP™ LUBRICOMP™ DX09407H compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Mpu0ag_LNP-LUBRICOMP-DX09407H-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP DX09407H is a compound based on High Heat Polycarbonate containing proprietary fillers. Added features of this grade are: Wear Resistant, Healthcare. Also known as: LNP* LUBRICOMP* Compound DX09407H Product reorder name: DX09407H |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.50 to 0.70 | % | |
| Across Flow : 24 hr | 0.60 to 0.80 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.21 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2230 | MPa | ASTM D638 |
| -- | 2130 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 64.0 | MPa | ASTM D638 |
| Yield | 64.0 | MPa | ISO 527-2/5 |
| Break 3 | 53.0 | MPa | ASTM D638 |
| Break | 56.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 6.8 | % | ASTM D638 |
| Yield | 6.9 | % | ISO 527-2/5 |
| Break 5 | 68 | % | ASTM D638 |
| Break | 110 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2310 | MPa | ASTM D790 |
| -- 7 | 2080 | MPa | ISO 178 |
| Flexural Strength 8(Break, 50.0 mm Span) | 90.0 | MPa | ASTM D790 |
| Flexural Strain at Break 9 | 77 | % | ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Linear Thermal Expansion - Flow (-30 to 100°C) | 7.40E-5 | µm/Mk | ISO 11359-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 140 | J/m | ASTM D256 |
| 23°C 10 | 11 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 2200 | J/m | ASTM D4812 |
| 23°C 11 | 190 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 139 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 137 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : -40 to 40°C | 7.4E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 7.7E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 48 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 271 to 293 | °C | |
| Middle Temperature | 282 to 304 | °C | |
| Front Temperature | 293 to 316 | °C | |
| Nozzle Temperature | 288 to 310 | °C | |
| Processing (Melt) Temp | 293 to 316 | °C | |
| Mold Temperature | 71.1 to 93.3 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 2 mm/min |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ULTEM™ 9090 resin | SABIC Innovative Plastics | PEI | ULTEM™ |
| Clariant Nylon 6 6253-L | Clariant Corporation | Nylon 6 | Clariant Nylon 6 |
| DURACON® M450-44 | Polyplastics Co., Ltd. | Acetal (POM) Copolymer | DURACON® |
| Karina CLEAR PVC COMPOUND -E 85/247-D-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Plaslube® PA6/6 T/AL20 HS | Techmer Engineered Solutions | Nylon 66 | Plaslube® |