Lion Idemitsu Composites PPS C-150SG
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Lion Idemitsu Composites Co., Ltd. |
| Trademark: | Lion Idemitsu Composites PPS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Mpbcd4_Lion-Idemitsu-Composites-PPS-C-150SG.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Lion Idemitsu Composites PPS C-150SG is a Polyphenylene Sulfide (PPS) product filled with 50% glass fiber. It is available in Asia Pacific. Primary characteristic: high strength. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.74 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow | 0.50 | % | |
| Flow | 0.40 | % | |
| Water Absorption (23°C, 24 hr) | > 0.020 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 101 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 196 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.6 | % | ISO 527-2 |
| Flexural Modulus | 17900 | MPa | ISO 178 |
| Flexural Stress | 289 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 16 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 273 | °C | ISO 75-2/A |
| CLTE | ISO 11359-2 | ||
| Flow | 1.5E-5 | cm/cm/°C | |
| Transverse | 4.5E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Electric Strength | IEC 60243-1 | ||
| 1.00 mm | 29 | kV/mm | |
| 3.00 mm | 13 | kV/mm | |
| Dielectric Constant | 4.10 | IEC 60250 | |
| Dissipation Factor | 2.0E-3 | IEC 60250 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flowability 2(1.00 mm) | 142 | mm | Internal Method |
| Note Message | |
|---|---|
| 1 . | Internal Method |
| 2 . | Thickness 1mm, Cylinder temperature 320°C, Injection pressure 100MPa, Mold temperature 135°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 2920-93 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| HI-ZEX™ 530B | Prime Polymer Co., Ltd. | HDPE | HI-ZEX™ |
| Karina BLUE PVC COMPOUND 900D06/469-AT-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Delene 5580 | Shanghai Lin Gen Rubber Materials Co., Ltd. | TPE | Delene |
| Sylvin 3220-55 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |