Westlake LDPE EF601
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Westlake Chemical Corporation |
| Trademark: | Westlake LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Mp3iGv_Westlake-LDPE-EF601.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Westlake EF601 is a fractional melt LDPE with excellent toughness. It is suggested in heavy duty films and shipping sacks, and in industrial shrink applications. It can be used as a bubble stabilizer in LLDPE rich films. Application/Uses: Heavy duty bags Heavy duty shipping sacks Industrial shrink film Heavy duty C&A sheeting |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.919 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.25 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | 0.50 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 51 | µm | |
| secant modulus 1 | ASTM D882 | ||
| 1% secant, MD : 51 µm, blown film | 152 | MPa | ASTM D882 |
| 1% secant, TD : 51 µm, blown film | 193 | MPa | ASTM D882 |
| Tensile Strength 2 | ASTM D882 | ||
| MD : Broken, 51 µm, blown film | 24.1 | MPa | ASTM D882 |
| TD : Broken, 51 µm, blown film | 18.6 | MPa | ASTM D882 |
| Tensile Elongation 3 | ASTM D882 | ||
| MD : Broken, 51 µm, blown film | 250 | % | ASTM D882 |
| TD : Broken, 51 µm, blown film | 750 | % | ASTM D882 |
| Dart Drop Impact 4(51 µm, Blown Film) | 500 | g | ASTM D1709 |
| Additional Information |
|---|
| Test specimens for blown film: nominal thickness 2.0 mils; blow up ratio 2.5:1, die gap 35 mils.Melt temperatures of 360° F - 400° F are recommended for Westlake Chemical EF601 with blow-up ratios of 1.5:1 or higher. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 182 - 204 | °C |
| Note Message | |
|---|---|
| 1 . | Test run at 23°C (73°F) and 50% relative humidity |
| 2 . | Test run at 23°C (73°F) and 50% relative humidity |
| 3 . | Test run at 23°C (73°F) and 50% relative humidity |
| 4 . | Test run at 23°C (73°F) and 50% relative humidity |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MegaCarb® 500-FR2 | Mega Polymers | PC | MegaCarb® |
| ACRYSTEX® PM-600 | CHI MEI CORPORATION | Acrylic (SMMA) | ACRYSTEX® |
| Dorlyl PVC GFB 60B | DORLYL S.N.C. | PVC, Unspecified | Dorlyl PVC |
| LightSpan® LS2-6941 | NuSil Technology | Silicone | LightSpan® |
| LUVOCOM® 1105-7173/BL | Lehmann & Voss & Co. | PEEK | LUVOCOM® |