Pro PP-HO-40T
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Pro Polymers |
| Trademark: | Pro-Comp™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MoYvMC_Pro-PP-HO-40T.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PP-HO-40T is a 40% Talc Filled, Polypropylene Homopolymer. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.26 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 3.18mm | 0.80 - 0.90 | % | ASTM D955 |
| Transverse flow : 3.18mm | 0.80 - 0.90 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 72 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 30.0 | MPa | ASTM D638 |
| Flexural Modulus | 3790 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 27 | J/m | ASTM D256 |
| Dart Drop Impact | 0.900 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 127 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 78.0 | °C | ASTM D648 |
| Additional Information |
|---|
| Melt Flow Rate, ASTM D1238, 230°C/2.1kgf: 8 to 12 g/10 min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Niretan B C30 | Soredi S.p.a. | Nylon 6 | Niretan B |
| Celcon® GC25T | Celanese Corporation | Acetal (POM) Copolymer | Celcon® |
| Kingfa JH830 | Kingfa | PC Alloy | Kingfa |
| Karina GRAY PVC COMPOUND -E 813-18/190-Y-RT-PO | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ THERMOTUF™ RF002I compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOTUF™ |