RTP 2581C HEC
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MnTGDS_RTP-2581C-HEC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. RTP 2580 C HEC Series material are polycarbonates/ABS alloys with nickel-coated carbon fiber added for electrical conductivity and EMI/RFI shielding. These materials are available in a range of colors. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.20 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6890 | MPa | ASTM D638 |
| Tensile Strength | 82.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.0 | % | ASTM D638 |
| Flexural Modulus | 5520 | MPa | ASTM D790 |
| Flexural Strength | 124 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 80 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 320 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 121 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+5 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+3 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm, RTP Tested) | HB | UL 94 |
| Additional Information |
|---|
| Shielding Effectiveness: 20+ dBStatic Decay, Mil B-81705C, FTMS-4046.1: <2.0 secondsThe Shielding Effectiveness testing was performed on edge-gated 6"x6"x0.090-0.120" panels, using NIST test cell per NBS Technical Note 1095. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 98.9 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 232 - 288 | °C | |
| Middle Temperature | 232 - 288 | °C | |
| Front Temperature | 232 - 288 | °C | |
| Mold Temperature | 71.1 - 98.9 | °C | |
| Injection Pressure | 68.9 - 103 | MPa | |
| Back Pressure | 0.345 | MPa | |
| Clamp Tonnage | 6.9 - 11 | kN/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTV-2 XP-643 | Silicones, Inc. | Silicone Rubber, RTV-2 | RTV-2 |
| Quadrant EPP Nylatron® LIG Nylon | Quadrant Engineering Plastic Products | Nylon 6 | Quadrant EPP |
| RheTech Polypropylene HP521-501UV | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| THERMOLAST® K TC8HAA (Series: AD/POM) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Osterlene® LL01020 | Osterman & Company | LLDPE | Osterlene® |