Axiall PVC 67800
| Category: | PVC, Flexible , Flexible Polyvinyl Chloride |
| Manufacturer: | Axiall Corporation |
| Trademark: | Axiall PVC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MnEEGG_AxiallPVC67800.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 67800 is a flexible extrusion PVC compound formulated for maximum service temperature of 90°C in both inner and outer Teck 90 jacketing applications. 67441 possesses exceptional low temperature properties to meet the -40°C low temperature impact and FT4 flame requirements. This compound is formulated to meet the optional listing of AG14. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.38 - 1.42 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 10 sec) | 76 - 82 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| -- | 17.7 | MPa | ASTM D638 |
| 100% strain | 9.58 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 290 | % | ASTM D638 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Ultimate Elongation in Air (121°C, 336 hr) | -26 | % | UL 1581 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -45.0 | °C | ASTM D746 |
| Melting Temperature | 182 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® HDPE CC253SL | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® HDPE |
| Sevrene® 3068-65A-0000 | Vi-Chem Corporation | TPE | Sevrene® |
| Sylvin 8318-70 White 1196 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| TUFNYL® SGF 30 BLUE | SRF Ltd. | Nylon 6 | TUFNYL® |
| FHR EPS 54-5654 | Flint Hills Resources, LP | PS (EPS) | FHR EPS |