Eltex® PF6212LJ is a metallocene LLDPE grade produced in Europe Benefits & Features Eltex® PF6212LJ is a polyethylene copolymer containing hexene-1 as the comonomer produced with a metallocene catalyst. It offers the following properties:
Applications Eltex® PF6212LJ has been developed for use in food packaging and other thin film applications where excellent mechanical and optical performance is required. In addition, Eltex® PF6212LJ is a version intended for lamination applications. If corona treatment is necessary, the level should normally be in the range 38-48 mN/m. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.920 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.3 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | < 0.25 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Tensile Modulus | ISO 527-3 | ||
| 1% Secant, MD : 25 µm | 180 | MPa | |
| 1% Secant, TD : 25 µm | 200 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 25 µm | 9.00 | MPa | |
| TD : Yield, 25 µm | 10.0 | MPa | |
| MD : Break, 25 µm | 65.0 | MPa | |
| TD : Break, 25 µm | 60.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 25 µm | 550 | % | |
| TD : Break, 25 µm | 670 | % | |
| Dart Drop Impact (25 µm) | > 1000 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm | 200 | g | |
| TD : 25 µm | 440 | g |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature 1 | 105 to 118 | °C | ASTM D3418 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.0 µm) | 62 | ASTM D2457 | |
| Haze (25.0 µm) | 8.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 to 230 | °C |
| Note Message | |
|---|---|
| 1 . | 2nd heating |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLAN T-05W | POLYMA Kunststoff GmbH & Co. KG | ABS | POLYLAN |
| Shin-Etsu Elastomer FEA-271U | Shin-Etsu Silicones of America | Fluoro Si | Shin-Etsu Elastomer |
| Tarflen® ST | Grupa Azoty S.A. | PTFE | Tarflen® |
| Nypol® PA A3 ST HS PRTA011 NR365 MSP | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Sylvin 9993-70 Grey 9609 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |