SCHULAMID® 612 FS 4003
| Category: | Nylon 612 , Polyamide 612 |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Mn5TpL_SCHULAMID-612-FS-4003.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Unfilled heat stabilizat nylon 612 compound |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.04 | -- | g/cm³ | ISO 1183/A |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 1750 | 750 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 46.0 | 34.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 5.0 | 25 | % | ISO 527-2/1A/50 |
| Nominal Tensile Strain at Break | > 100 | > 300 | % | ISO 527-2/1A/50 |
| Flexural Modulus 1 | 1250 | -- | MPa | ISO 178 |
| Flexural Stress 2 | 52.0 | -- | MPa | ISO 178 |
| Flexural Strain at Flexural Strength | 8.00 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 30 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 98 kJ/m² | No Break | ISO 179/1eA | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | -- | ISO 179/1eU | |
| 23°C | No Break | No Break | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 145 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 60.0 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | ||||
| -- | 200 | -- | °C | ISO 306/A50 |
| -- | 140 | -- | °C | ISO 306/B50 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate (2.00 mm) | < 20 | -- | mm/min | ISO 3795 |
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 1.50 mm | HB | -- | IEC 60695-11-10, -20 | |
| 3.00 mm | HB | -- | IEC 60695-11-10, -20 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 1.50 mm | 725 | -- | °C | IEC 60695-2-12 |
| 3.00 mm | 725 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 1.50 mm | 750 | -- | °C | IEC 60695-2-13 |
| 3.00 mm | 750 | -- | °C | IEC 60695-2-13 |
| Additional Information |
|---|
| 干燥 ISO 1874-PA 612-EAGHLW-18-020-NDIN73378-PA 612-HIHL |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Milastomer™ 5517BS | Mitsui Chemicals America, Inc. | TPV | Milastomer™ |
| Zytel® 158L NC010 | DuPont Performance Polymers | Nylon 612 | Zytel® |
| BJB Polyurethane TC-885 FR REV 1 | BJB Enterprises, Inc. | PUR, Unspecified | BJB Polyurethane |
| Ecomass® 720ZC85 | Ecomass Technologies | ABS | Ecomass® |
| INEOS PP 200-NA02 | INEOS Olefins & Polymers Europe | PP Random Copolymer | INEOS PP |