UTTAP QU HT530 GF
| Category: | Nylon, Unspecified , Polyamide |
| Manufacturer: | Ovation Polymers Inc. |
| Trademark: | UTTAP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MkKtdh_UTTAP-QU-HT530-GF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Glass reinforced (30 %) - High Temperature Polyamide Alloy, excellent chemical and electrical resistance, high stiffness, modulus and HDT. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.48 | g/cm³ | ASTM D792 |
| Water Absorption (24 hr) | 0.80 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 6000 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 160 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 3.5 | % | ASTM D638 |
| Flexural Modulus 4(50.0 mm Span) | 10500 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 50.0 mm Span) | 205 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 70 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 220 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 218 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Salflex 830I | Salflex Polymers Ltd. | PP, Unspecified | Salflex |
| Selvol™ ULTALUX FA | Sekisui Chemical Company, Ltd. | PVOH | Selvol™ |
| THERMOLAST® K TC5PCZ (Series: AD/PA/CS) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Nypol® PA B3 HF CNZA011 NT384 | Petropol Industry and Trade of Polymers LTDA | Nylon 6 | Nypol® PA |
| Dow Corning® C6-150 | Dow Corning Corporation | Silicone | Dow Corning® |