Romiloy® 1015/01 F
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | ROMIRA GmbH |
| Trademark: | Romiloy® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MiU6g9_Romiloy-1015-01-F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Romiloy®1015/01 F is a polycarbonate acrylonitrile butadiene styrene (PC ABS) material,. This product is available in Europe and is processed by extrusion or injection molding. Romiloy®The main features of 1015/01 F are:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.15 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 20 | g/10 min | ISO 1133 |
| Molding Shrinkage (23°C) | 0.40 - 0.70 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2250 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 58.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 23°C) | 50 | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C) | 2270 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 88.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 20 | kJ/m² | ISO 179/1eA |
| 23°C | 35 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 105 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 130 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Additional Information |
|---|
| The value listed as Molding Shrinkage ISO 294-4, was tested in accordance with DIN 16901.Tensile Strain at Break, ISO 527-1-2, 23°C, 50 mm/min: >50% |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 100 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Suggested Max Regrind | 5 | % | |
| Processing (Melt) Temp | 240 - 270 | °C | |
| Mold Temperature | 80.0 | °C | |
| Injection Rate | Moderate-Fast |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 100 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Cylinder Zone 1 Temp. | 210 - 250 | °C | |
| Cylinder Zone 2 Temp. | 210 - 250 | °C | |
| Cylinder Zone 3 Temp. | 210 - 250 | °C | |
| Cylinder Zone 4 Temp. | 210 - 250 | °C | |
| Cylinder Zone 5 Temp. | 210 - 250 | °C | |
| Melt Temperature | < 260 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Andur 850 AP | Anderson Development Company | PUR-Est/eth,TDI | Andur |
| Cheng Yu FV30G15 | Cheng Yu Plastic Company Limited | Acetal (POM) Homopolymer | Cheng Yu |
| Haysite SMC 42000 | Haysite Reinforced Plastics | Polyester, TS | Haysite SMC |
| Hylon® N2213THL | Ravago Manufacturing Americas, LLC | Nylon 6 | Hylon® |
| POLYCASA® ACRYL G 88 E | Polycasa | Acrylic (PMMA) | POLYCASA® ACRYL |