ASTAMID™ MB3G6HS
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | ASTAMID™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Mi2Ag2_ASTAMID-MB3G6HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ASTAMID™ MB3G6HS is a highly heat stabilised 30% glass fibre reinforced Polyamide 6 grade. ASTAMID™ MB3G6HS has been developed for structural applications within the automotive sector. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.36 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.40 | -- | % | ASTM D955 |
| Water Absorption | ||||
| Saturated, 23°C | 6.5 | -- | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 2.1 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus 1(3.20 mm) | 9500 | 6200 | MPa | ASTM D638 |
| Tensile Strength 2(3.20 mm) | 185 | 115 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, 3.20 mm) | 4.0 | 8.0 | % | ASTM D638 |
| Flexural Modulus 4(3.20 mm) | 8600 | 5000 | MPa | ASTM D790 |
| Flexural Strength 5(3.20 mm) | 270 | 190 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength 6 | 16 | 30 | kJ/m² | ISO 179 |
| Notched Izod Impact (3.20 mm) | 150 | 210 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, unannealed, 3.20mm | 220 | -- | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 210 | -- | °C | ASTM D648 |
| CLTE - Flow | 3.5E-5 | -- | cm/cm/°C | ASTM D696 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 90.0 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 255 - 265 | °C | |
| Middle Temperature | 265 - 275 | °C | |
| Front Temperature | 275 - 285 | °C | |
| Processing (Melt) Temp | 260 - 290 | °C | |
| Mold Temperature | 50.0 - 80.0 | °C | |
| Injection Pressure | 60.0 - 130 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.100 - 0.500 | MPa | |
| Screw Speed | 40 - 60 | rpm | |
| Clamp Tonnage | 3.0 - 5.0 | kN/cm² |
| Injection instructions |
|---|
| Drying Time: >12 hr for already open bag |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V191A NAT601 FR | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Braskem PP RP 340S | Braskem | PP Random Copolymer | Braskem PP |
| Fortron® 6450A6 | Celanese Corporation | PPS | Fortron® |
| StarGrip-X® 5055-1000 | Star Thermoplastic Alloys & Rubbers, Inc. | TPE | StarGrip-X® |
| POCAN® A 3121 000000 | LANXESS GmbH | PBT+ASA | POCAN® |