Tenite™ Acetate 105E3V36327 Clear, Trsp
| Category: | CA , Cellulose Acetate |
| Manufacturer: | Eastman Chemical Company |
| Trademark: | Tenite™ Acetate |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MhtU60_Tenite-Acetate-105E3V36327-Clear-Trsp.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Tenite™ cellulosic plastics are noted for their excellent balance of properties - toughness, hardness, strength, surface gloss, clarity, and a warm feel. The mechanical properties if Tenite™ cellulosic plastics differ with plasticizer levels. Lower plasticizer content yields a harder surface, higher heat resistance, greater rigidity, higher tensile strength, and better dimensional stability. Higher plasticizer content increases impact strength. Tenite™ cellulosic plastics are available in natural, clear, selected ambers or smoke transparents and black translucent. Color concentrates are available in let-down ratios from 10:1 to 40:1. Tenite™ Cellulosic Acetate 105-27 has a plasticizer level of 27%. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.28 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.20 to 0.60 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 2.3 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 82 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 23°C | 33.1 | MPa | |
| Break, 23°C | 36.5 | MPa | |
| Tensile Elongation (Break, 23°C) | 25 | % | ASTM D638 |
| Flexural Modulus (23°C) | 2140 | MPa | ASTM D790 |
| Flexural Strength (Yield, 23°C) | 54.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C | 48 | J/m | |
| 23°C | 190 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 1 | ASTM D648 | ||
| 0.45 MPa, Annealed | 83.0 | °C | |
| 1.8 MPa, Annealed | 73.0 | °C | |
| Vicat Softening Temperature 2 | 109 | °C | ASTM D1525 |
| CLTE - Flow (23°C) | 2.0E-5 | cm/cm/°C | ASTM D696 |
| Specific Heat (23°C) | 1260 to 1670 | J/kg/°C | DSC |
| Thermal Conductivity 3(23°C) | 0.25 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (23°C) | 12 to 19 | kV/mm | ASTM D149 |
| Dielectric Constant (23°C, 1 MHz) | 3.30 to 3.80 | ASTM D150 | |
| Dissipation Factor (23°C, 1 MHz) | 0.010 to 0.15 | ASTM D150 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.460 to 1.490 | ASTM D542 | |
| Transmittance (1520 µm) | > 90.0 | % | ASTM D1003 |
| Haze (1520 µm) | < 8.5 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Soluble Matter Loss (23°C) | 0.30 | % | ASTM D570 |
| Weight Loss on Heating - 72 hrs (80°C) | 1.8 | % | ASTM D706 |
| Note Message | |
|---|---|
| 1 . | Conditioned 4 hours at 70°C (158°F) |
| 2 . | Conditioned 4 hours at 70°C (158°F) |
| 3 . | Range: 0.17 to 0.33 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VENYL SWGB307H | AD majoris | Nylon 6 | VENYL |
| TOTAL Polyethylene HD 6081 | TOTAL Refining & Chemicals | HDPE | TOTAL Polyethylene |
| Ultraform® W 2320 003 UNC Q600 | BASF Corporation | Acetal (POM) Copolymer | Ultraform® |
| Celstran® PP-GF50-0453 P10/10 | Celanese Corporation | PP, Unspecified | Celstran® |
| Plaslube® TPU 40D GL10 | Techmer Engineered Solutions | TPU, Unspecified | Plaslube® |