DOWLEX™ 2111GC
| Category: | LLDPE , Linear Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOWLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MhggWg_DOWLEX-2111GC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DOWLEX™ 2111GC Polyethylene Resin is specifically designed for large/high output cast film lines to make high performance industrial stretch films. Films made from DOWLEX 2111GC Polyethylene Resin exhibit an excellent balance of processability, mechanical and stretchability performance properties. DOWLEX 2111GC Polyethylene Resin is to be used as a core resin in coextruded cast film structures together with a cling resin for films in the thickness range between 10 and 35 microns. Applications:
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.920 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.7 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 23 | µm | |
| Film Puncture Force 1(23 µm) | 31.0 | N | Internal method |
| Tensile Stress 2 | ISO 527-3 | ||
| MD : Yield, 23 µm | 5.80 | MPa | ISO 527-3 |
| TD : Yield, 23 µm | 6.00 | MPa | ISO 527-3 |
| MD : Break, 23 µm | 34.0 | MPa | ISO 527-3 |
| TD : Break, 23 µm | 25.0 | MPa | ISO 527-3 |
| Tensile Elongation 3 | ISO 527-3 | ||
| MD : Break, 23 µm | 430 | % | ISO 527-3 |
| TD : Break, 23 µm | 690 | % | ISO 527-3 |
| Dart Drop Impact 4(23 µm) | 110 | g | ISO 7765-1/A |
| Elmendorf Tear Strength 5 | ASTM D1922 | ||
| MD : 23 µm | 170 | g | ASTM D1922 |
| TD : 23 µm | 550 | g | ASTM D1922 |
| Film tensile properties-maximum tensile force 6(23.0 µm) | 36000 | g | Internal method |
| Film Tensile Properties-Maximum Elongation 7(23.0 µm) | 350 | % | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss 8(45°, 23.0 µm) | 93 | ASTM D2457 | |
| Haze 9(23.0 µm) | 0.60 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 250 | °C |
| Extrusion instructions |
|---|
| Fabrication Conditions For Cast Films: Chill Roll Temperature: 25°C Melt Temperature: 250°C Recommended Gauge Range: 10 to 35 µm |
| Note Message | |
|---|---|
| 1 . | Cast film fabricated at 250 m/min |
| 2 . | Cast film fabricated at 250 m/min |
| 3 . | Cast film fabricated at 250 m/min |
| 4 . | Cast film fabricated at 250 m/min |
| 5 . | Cast film fabricated at 250 m/min |
| 6 . | Cast film fabricated at 250 m/min |
| 7 . | Cast film fabricated at 250 m/min |
| 8 . | Cast film fabricated at 250 m/min |
| 9 . | Cast film fabricated at 250 m/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 899 X 93924 | RTP Company | Acetal (POM) Copolymer | RTP |
| Andur 75 DGP 2 | Anderson Development Company | PUR-Ether/TDI | Andur |
| Evoprene™ G 971 | AlphaGary | SEBS | Evoprene™ G |
| DuraElast 1516 | Evermore Chemical Industry Co., Ltd. | TPU-Polyether | DuraElast |
| Hostacom TRC 333N D72714 | LyondellBasell Industries | PP Copolymer | Hostacom |