VALOX™ EH7020 resin
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Mh1V3S_VALOX-EH7020-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| MINERAL FILLED, METALLIZABLE |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.49 | g/cm³ | ASTM D792 |
| Molding Shrinkage | Internal Method | ||
| Flow 1 | 1.4 to 1.6 | % | |
| Flow 2 | 1.5 to 1.6 | % | |
| Across Flow 3 | 1.3 to 1.4 | % | |
| Across Flow 4 | 1.4 to 1.5 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 5(Break) | 57.9 | MPa | ASTM D638 |
| Flexural Modulus 6(50.0 mm Span) | 4140 | MPa | ASTM D790 |
| Flexural Strength 7(Break, 50.0 mm Span) | 103 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 32 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 390 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 188 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 105 | °C | |
| CLTE - Flow (-40 to 40°C) | 5.6E-5 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (3.20 mm, in Oil) | 17 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 50 Hz | 3.10 | ||
| 60 Hz | 3.10 | ||
| 1 MHz | 2.90 | ||
| Dissipation Factor | ASTM D150 | ||
| 50 Hz | 3.9E-3 | ||
| 60 Hz | 3.9E-3 | ||
| 1 MHz | 0.014 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 12 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 80 | % | |
| Rear Temperature | 238 to 254 | °C | |
| Middle Temperature | 243 to 260 | °C | |
| Front Temperature | 249 to 266 | °C | |
| Nozzle Temperature | 243 to 260 | °C | |
| Processing (Melt) Temp | 249 to 266 | °C | |
| Mold Temperature | 65.6 to 87.8 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 50 to 80 | rpm | |
| Vent Depth | 0.025 to 0.038 | mm |
| Note Message | |
|---|---|
| 1 . | 1.5 to 3.2 mm |
| 2 . | 3.2 to 4.6 mm |
| 3 . | 1.5 to 3.2 mm |
| 4 . | 3.2-4.6 mm |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Propafilm™ MVG120 | Innovia Films Ltd. | PP Alloy | Propafilm™ |
| VITAMIDE® BX30WT6617 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| Delta ATL C9-U6 | Delta Polymers | Acetal (POM) Copolymer | Delta |
| K-vinyl 20 A 75 | Technovinyl Polymers India Ltd. | PVC, Unspecified | K-vinyl |
| LEXAN™ 945A resin | SABIC Innovative Plastics | PC | LEXAN™ |