Latamid 12 H2 G/30
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latamid |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MgyChT_Latamid-12-H2-G-30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Polyamide 12 (PA 12). Heat stabilised. Glass fibres. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.23 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.80 to 1.1 | % | |
| Flow : 2.00 mm | 0.40 to 0.70 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 6600 | MPa | |
| 60°C | 4000 | MPa | |
| 90°C | 3200 | MPa | |
| 120°C | 2700 | MPa | |
| 150°C | 2100 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 23°C | 100 | MPa | |
| Yield, 60°C | 75.0 | MPa | |
| Yield, 90°C | 60.0 | MPa | |
| Yield, 120°C | 50.0 | MPa | |
| Yield, 150°C | 35.0 | MPa | |
| Break, 23°C | 100 | MPa | |
| Break, 60°C | 75.0 | MPa | |
| Break, 90°C | 60.0 | MPa | |
| Break, 120°C | 50.0 | MPa | |
| Break, 150°C | 35.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 23°C | 7.0 | % | |
| Yield, 60°C | > 10 | % | |
| Yield, 90°C | > 10 | % | |
| Yield, 120°C | > 10 | % | |
| Yield, 150°C | > 10 | % | |
| Break, 23°C | 8.0 | % | |
| Break, 60°C | 11 | % | |
| Break, 90°C | 12 | % | |
| Break, 120°C | 14 | % | |
| Break, 150°C | 16 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 10 | kJ/m² | |
| 23°C | 15 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 80 | kJ/m² | |
| 23°C | 70 | kJ/m² | |
| Notched Izod Impact (23°C, 3.20 mm) | 130 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 180 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 175 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 120 | °C | |
| Vicat Softening Temperature | 170 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 1.0E-5 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 210 to 230 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 MPa of cavity pressure |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reslen PPH 20GF GWT 960 | Polimarky Spolka Jawna | PP Homopolymer | Reslen |
| TAIRILAC AG12A3 | Formosa Plastics Corporation | ABS | TAIRILAC |
| TRISTAR® PC-10R-(V20) | Polymer Technology and Services, LLC | PC | TRISTAR® |
| KPOL-PP K-PPH 2.1 S | KPOL Chem Co. | PP Homopolymer | KPOL-PP |
| Sylvin 7833-75 Grey 9280 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |