Ultramid 8234G HS is a heat stabilized, 44% glass fiber reinforced PA6 injection molding compound offering the highest level of strength, stiffness, high temperature performance and dimensional stability. It is available in natural and black versions. Pigmented and weatherable versions may be offered on a case by case fbasis. Applications Ultramid 8234G HS is generally recommended for applications such as power tool housings, cattle ear taggers, luggage frames, fans and pressure regulator housings.

General Information
Filler / Reinforcement	Glass Fiber, 44% Filler by Weight
Additive	Heat Stabilizer
Features	Good Dimensional Stability Heat Stabilized High Heat Resistance High Stiffness High Strength
Uses	Housings Luggage Molded Ear Tags Power/Other Tools
Agency Ratings	EC 1907/2006 (REACH)
RoHS Compliance	RoHS Compliant
Appearance	Black Colors Available Natural Color
Forms	Pellets
Processing Method	Injection Molding

Physical	Dry	Conditioned	Unit	Test Method
Specific Gravity	1.49	--	g/cm³	ASTM D792, ISO 1183
Molding Shrinkage - Flow (3.18 mm)	0.20	--	%
Water Absorption
24 hr	0.90	--	%	ASTM D570
23°C, 24 hr	0.90	--	%	ISO 62
Saturation	5.2	--	%	ASTM D570
Saturation, 23°C	5.2	--	%	ISO 62
Equilibrium, 50% RH	1.5	--	%	ASTM D570
Equilibrium, 23°C, 50% RH	1.5	--	%	ISO 62

Hardness	Dry	Conditioned	Unit	Test Method
Rockwell Hardness (R-Scale)	121	--		ASTM D785

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus (23°C)	13500	7490	MPa	ISO 527-2
Tensile Strength
Break, 23°C	230	145	MPa	ASTM D638
Break, 23°C	215	145	MPa	ISO 527-2
Tensile Elongation
Break, 23°C	2.0	6.0	%	ASTM D638
Break, 23°C	3.0	6.0	%	ISO 527-2
Flexural Modulus
-40°C	12300	14700	MPa	ASTM D790
23°C	11700	6560	MPa	ASTM D790
65°C	7000	--	MPa	ASTM D790
121°C	4830	--	MPa	ASTM D790
23°C	11400	--	MPa	ISO 178
Flexural Strength
-40°C	450	410	MPa	ASTM D790
23°C	352	212	MPa	ASTM D790
65°C	220	--	MPa	ASTM D790
90°C	160	--	MPa	ASTM D790
121°C	138	--	MPa	ASTM D790
23°C	325	--	MPa	ISO 178

Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength (23°C)	21	--	kJ/m²	ISO 179
Charpy Unnotched Impact Strength (23°C)	90	--	kJ/m²	ISO 179
Notched Izod Impact
23°C	130	--	J/m	ASTM D256
-40°C	11	--	kJ/m²	ISO 180
23°C	14	--	kJ/m²	ISO 180
Drop Impact Resistance (23°C)	4.07	--	J	Internal Method

Thermal	Dry	Conditioned	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, Unannealed	220	--	°C	ISO 75-2/B
1.8 MPa, Unannealed	212	--	°C	ASTM D648
1.8 MPa, Unannealed	210	--	°C	ISO 75-2/A
Peak Melting Temperature	220	--	°C	ASTM D3418, ISO 3146
CLTE
Flow	3.1E-5	--	cm/cm/°C	ASTM E831
Flow	3.2E-5	--	cm/cm/°C
Transverse	7.9E-5	--	cm/cm/°C
RTI Elec				UL 746
0.710 mm	130	--	°C
1.50 mm	140	--	°C
3.00 mm	140	--	°C
RTI Imp				UL 746
0.710 mm	95.0	--	°C
1.50 mm	105	--	°C
3.00 mm	105	--	°C
RTI Str				UL 746
0.710 mm	130	--	°C
1.50 mm	140	--	°C
3.00 mm	140	--	°C

Flammability	Dry	Conditioned	Test Method
Flame Rating			UL 94
1.50 mm	HB	--
3.00 mm	HB	--

Category:	Nylon 6 , Polyamide 6
Manufacturer:	BASF Corporation
Trademark:	Ultramid®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	MgpYFU_Ultramid-8234G-HS.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Sarlink® TPV 3135	Teknor Apex Company	TPV	Sarlink® TPV
THERMOLAST® K TF9BNA (Series: FC/AP)	KRAIBURG TPE	TPE	THERMOLAST® K
Bergamid鈩?A70 G25 H natur TM-X	PolyOne Corporation	Nylon 66	Bergamid™
APEX® 84853-L	Teknor Apex Company	PVC, Flexible	APEX®
Grilon® CA 6 E	EMS-GRIVORY	Nylon 6/12	Grilon®