Rotec® ABS 5001
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | ROMIRA GmbH |
| Trademark: | Rotec® ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MglmvY_Rotec-ABS-5001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Rotec®ABS 5001 is an acrylonitrile butadiene styrene (ABS) material,. This product is available in Europe and is processed by extrusion or injection molding. Rotec®The main features of ABS 5001 are:
|
| General Information | |
|---|---|
| Features |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 18 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.50 - 0.70 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.30 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2100 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 45.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 23°C) | 20 | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C) | 2200 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 70.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 21 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 97.0 | °C | ISO 306/B50 |
| CLTE - Flow (23 to 55°C) | 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.17 | W/m/K | ISO 8302 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Additional Information |
|---|
| The value listed as Thermal Conductivity ISO 8302, was tested in accordance with DIN 52612. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Suggested Max Regrind | 5 | % | |
| Rear Temperature | 210 - 250 | °C | |
| Middle Temperature | 210 - 250 | °C | |
| Front Temperature | 210 - 250 | °C | |
| Processing (Melt) Temp | < 260 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C | |
| Injection Rate | Fast |
| Injection instructions |
|---|
| Screw rotation speed: moderate to highBack pressure: low to moderateInjection pressure: tool depending |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Cylinder Zone 1 Temp. | 190 - 210 | °C | |
| Cylinder Zone 2 Temp. | 190 - 210 | °C | |
| Cylinder Zone 3 Temp. | 190 - 210 | °C | |
| Cylinder Zone 4 Temp. | 190 - 210 | °C | |
| Cylinder Zone 5 Temp. | 190 - 210 | °C | |
| Melt Temperature | < 245 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polytron® P40N011 | Polyram Ram-On Industries | PP Homopolymer | Polytron® |
| Silopren® LSR 2540 | Momentive Performance Materials Inc. | Silicone Rubber, LSR | Silopren® |
| Spartech Polycom SCR7F-7015UR | Spartech Polycom | PC | Spartech |
| Ultraclear™ 480 | Hapco Inc. | TP, Unspecified | Ultraclear™ |
| BP PPC 0218-22 BLK | Buckeye Polymers, Inc. | PP Copolymer | BP |