ASTALAC™ ABS M112
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | ASTALAC™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MgdzTa_ASTALAC-ABS-M112.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ASTALAC™ ABS M112 is an ultra high heat resistance grade of ABS and is designed for injection moulding applications requiring a balance of high heat resistance, impact toughness, product rigidity and mouldability. Typical applications in the automotive area include interior air vents, console mouldings, T-Bar surround assemblies and coloured interior doorhandles. Note: The letters "UV" or "W" indicate UV stabilisation has been added [ ie: ASTALAC™ ABS M112UV ]. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 220°C/10.0 kg | 5.0 | g/10 min | |
| 230°C/3.8 kg | 2.0 | g/10 min | |
| Molding Shrinkage - Flow (3.00 mm) | 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.25 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 108 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.20 mm) | 50.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 40 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2450 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 75.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 150 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, Unannealed, 3.20 mm | 90.0 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 96.0 | °C | |
| 1.8 MPa, Unannealed, 12.7 mm | 105 | °C | |
| Vicat Softening Temperature | 118 | °C | ASTM D1525 5 |
| CLTE - Flow | 8.5E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (1.60 mm) | 550 | °C | AS/NZS 60695.2.12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 95.0 | °C | |
| Drying Time | 3.0 to 6.0 | hr | |
| Rear Temperature | 215 to 235 | °C | |
| Middle Temperature | 225 to 245 | °C | |
| Front Temperature | 235 to 255 | °C | |
| Processing (Melt) Temp | 230 to 260 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C | |
| Injection Pressure | 60.0 to 140 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.100 to 0.500 | MPa | |
| Screw Speed | 40 to 60 | rpm | |
| Clamp Tonnage | 3.0 to 6.0 | kN/cm² |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1383 TFE 15 | RTP Company | PPS | RTP |
| NatureFlex™ 45NVL | Innovia Films Ltd. | Cellulose, Regenerated | NatureFlex™ |
| DJSilicone NE-141 | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| Sylvin 9710-80FUV Orange 574 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| CYCOLAC™ INP563 resin | SABIC Innovative Plastics | ABS+SAN | CYCOLAC™ |