DENYL 66 0037 H
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Vamp Tech |
| Trademark: | DENYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MgMbhl_DENYL-66-0037-H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 66, with elastomer, not Flame Retardant compound, good impact resistance. |
| General Information | |
|---|---|
| Features |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.11 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | |||
| Flow | 1.6 | -- | % | |
| Across Flow | 1.6 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2300 | -- | MPa | ASTM D638 |
| Tensile Strength | ||||
| Yield | 60.0 | 42.0 | MPa | ASTM D638 |
| Yield | -- | 42.0 | MPa | ISO 527-2 |
| Tensile Elongation | ||||
| Yield | -- | 180 | % | ASTM D638, ISO 527-2 |
| Break | > 20 | -- | % | ASTM D638 |
| Flexural Modulus | -- | 1000 | MPa | ASTM D790, ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact Strength | 13 | -- | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength | No Break | -- | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 70.0 | -- | °C | ASTM D648A |
| Vicat Softening Temperature | 215 | -- | °C | ASTM D1525 1 |
| RTI Elec | 100 | -- | °C | UL 746 |
| RTI Imp | 100 | -- | °C | UL 746 |
| RTI Str | 100 | -- | °C | UL 746 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index (CTI) | 600 | -- | V | UL 746 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 270 | °C | |
| Mold Temperature | 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| BESTNYL SI20VI01AHQ03 | Triesa Plastics | Nylon 6 | BESTNYL |
| Edgetek™ ET3200-8001 LG | PolyOne Corporation | PC | Edgetek™ |
| INTOL® 1783 | Versalis S.p.A. | SBR, Emulsion | INTOL® |
| Karina CLEAR PVC COMPOUND -E 80/229-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PEARLSTICK® 48-60/03 | Lubrizol Advanced Materials, Inc. | TPU-Polyester | PEARLSTICK® |