UmaPET CO/CI Datasheet,PET,Ester Industries Ltd.-SHANGHAI SUSHENG

Message
KEY FEATURES UmaPET CO/CI has good transparency, excellent machinability, high gloss and flexibility. One side corona treatment for improvement in adhesion to inks, adhesives and metal in metallization. The film possesses good thermal, mechanical, optical and surface properties along with excellent transparency and dimensional stability. APPLICATIONS The film is designed for use in printing, metallizing, coating and lamination processes widely for flexible packaging applications.

General Information
Features	Excellent Printability Good Adhesion Good Dimensional Stability Good Flexibility Good Surface Finish High Clarity High Gloss Machinable Metallizable Opticals
Uses	Coating Applications Film Laminates Packaging
Appearance	Clear/Transparent
Forms	Film

Physical	Nominal Value	Unit	Test Method
Molding Shrinkage			ASTM D1204
Flow : 150°C, 30 min, 0.0100 mm	2.5	%
Flow : 150°C, 30 min, 0.0120 mm	2.5	%
Flow : 150°C, 30 min, 0.0150 mm	2.5	%
Flow : 150°C, 30 min, 0.0230 mm	2.5	%
Across Flow : 150°C, 30 min, 0.0100 mm	0.40	%
Across Flow : 150°C, 30 min, 0.0120 mm	0.40	%
Across Flow : 150°C, 30 min, 0.0150 mm	0.40	%
Across Flow : 150°C, 30 min, 0.0230 mm	0.40	%

Mechanical	Nominal Value	Test Method
Coefficient of Friction		ASTM D1894
vs. Itself - Dynamic ¹	0.48
vs. Itself - Dynamic ²	0.48
vs. Itself - Dynamic ³	0.48
vs. Itself - Dynamic ⁴	0.44
vs. Itself - Static ⁵	0.54
vs. Itself - Static ⁶	0.54
vs. Itself - Static ⁷	0.54
vs. Itself - Static ⁸	0.50

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	10 12 15 23	µm
Film Thickness - Recommended / Available	10, 12, 15, 23 µm
Tensile Strength			ASTM D882
MD : Break, 10 µm	206	MPa
MD : Break, 12 µm	206	MPa
MD : Break, 15 µm	186	MPa
MD : Break, 23 µm	186	MPa
TD : Break, 10 µm	216	MPa
TD : Break, 12 µm	216	MPa
TD : Break, 15 µm	206	MPa
TD : Break, 23 µm	206	MPa
Tensile Elongation			ASTM D882
MD : Break, 10 µm	100	%
MD : Break, 12 µm	100	%
MD : Break, 15 µm	100	%
MD : Break, 23 µm	100	%
TD : Break, 10 µm	90	%
TD : Break, 12 µm	90	%
TD : Break, 15 µm	90	%
TD : Break, 23 µm	90	%
Yield			Internal Method
10.0 µm	71.4	m²/kg
12.0 µm	59.5	m²/kg
15.0 µm	47.6	m²/kg
23.0 µm	31.0	m²/kg

Additional Information	Nominal Value	Unit	Test Method
Wetting Tension			ASTM D2578
Coated side : 10.0 µm	52	dyne/cm
Coated side : 12.0 µm	52	dyne/cm
Coated side : 15.0 µm	52	dyne/cm
Coated side : 23.0 µm	52	dyne/cm
Plain side : 10.0 µm	44	dyne/cm
Plain side : 12.0 µm	44	dyne/cm
Plain side : 15.0 µm	44	dyne/cm
Plain side : 23.0 µm	44	dyne/cm

Optical	Nominal Value	Unit	Test Method
Haze			ASTM D1003
10.0 µm	3.5	%
12.0 µm	3.5	%
15.0 µm	3.5	%
23.0 µm	4.5	%

Category:	PET , Polyethylene Terephthalate
Manufacturer:	Ester Industries Ltd.
Trademark:	UmaPET
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	MgEar5_UmaPET-CO-CI.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Tempalux® 5000	Westlake Plastics Company	PEI	Tempalux®
Zytel® FG42A NC010	DuPont Performance Polymers	Nylon 66	Zytel®
DOW™ LDPE 955I	The Dow Chemical Company	LDPE	DOW™ LDPE
Eleme HFG00346	Eleme Petrochemical Company Ltd	HDPE	Eleme
Sylvin 8260-85UV Blue 8439	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin