EL-Lene™ H5211PC
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | SCG Chemicals Co., Ltd. |
| Trademark: | EL-Lene™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MfNVnV_EL-Lene-H5211PC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EL-Lene H5211PC is a black, bimodal technology, high density polyethylene compound classified as a MRS 8.0 material (PE80) providing superior in mechanical properties and processablity. EL-Lene H5211PC also shows excellent resistance to rapid crack propagation and slow crack growth. In addition, It includes a good dispersion of carbon black pigment and anti-oxidant to ensure excellent long term in UV resistance and thermal stability. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.960 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/5.0 kg) | 0.40 | g/10 min | ISO 1133 |
| Environmental Stress-Cracking Resistance (F0) | > 10000 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 62 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/100 | ||
| Yield | 22.0 | MPa | ISO 527-2/100 |
| Fracture | 33.0 | MPa | ISO 527-2/100 |
| Tensile Strain (Break) | 810 | % | ISO 527-2/100 |
| Flexural Modulus | 980 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -20°C | 8.0 | J/m | ASTM D256 |
| 0°C | 160 | J/m | ASTM D256 |
| 23°C | 200 | J/m | ASTM D256 |
| Additional Information |
|---|
| Oxidation induction time, ISO/TR10837, 20°C: >50 minMRS, ISO TR9080: 8 MPaResistance to slow crack grwoth, ISO 13479, 80°C: >500 hrsRapid crack propagation, ISO 13477: >8 barResistance to gas constituents, ISO 1167: >20 hrsCarbon Black Content, ISO 6964: 2.3% wt |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 90.0 | °C | |
| Drying Time | 1.0 - 2.0 | hr | |
| Melt Temperature | 170 - 200 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makropol® PC A3 G20 PRTA010 PC315 | Petropol Industry and Trade of Polymers LTDA | PC | Makropol® PC |
| Maxelast® A9840 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Moplen EP442M | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| Crastin® SK695FR NC010 | DuPont Performance Polymers | PBT | Crastin® |
| Elastron® G G300.A55.N | Elastron USA, Inc. | SEBS | Elastron® G |