KumhoSunny PC/PBT HCB9230
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | Shanghai KumhoSunny Plastics Co., Ltd. |
| Trademark: | KumhoSunny PC/PBT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MfFpVc_KumhoSunny-PC-PBT-HCB9230.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HCB9230 is a high flow and high heat resistance PC/PBT alloy resin, offering high impact and good chemical resistance.HCB9230 is recommended for auto outside laggage carrier,handle, ectron & electric parts etc. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 250°C/5.0 kg | 13 | g/10 min | ASTM D1238 |
| 250°C/5.0 kg | 15 | g/10 min | ISO 1133 |
| Molding Shrinkage | |||
| Flow | 0.60 to 0.90 | % | ASTM D955 |
| -- | 0.60 to 0.90 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| -- | 63.0 | MPa | ASTM D638 |
| -- | 56.0 | MPa | ISO 527-2/50 |
| Tensile Elongation (Break) | 120 | % | ASTM D638 |
| Flexural Modulus | |||
| -- | 2200 | MPa | ASTM D790 |
| -- 1 | 2100 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 87.0 | MPa | ASTM D790 |
| -- 2 | 80.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 30 | kJ/m² | |
| 23°C | 55 | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179 | |
| Notched Izod Impact | |||
| 3.20 mm | 820 | J/m | ASTM D256 |
| 23°C | 55 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed | 107 | °C | ASTM D648 |
| 1.8 MPa, Unannealed 3 | 98.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 115 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 110 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | < 0.020 | % | |
| Rear Temperature | 230 to 260 | °C | |
| Middle Temperature | 240 to 270 | °C | |
| Front Temperature | 240 to 270 | °C | |
| Nozzle Temperature | 245 to 265 | °C | |
| Processing (Melt) Temp | 240 to 270 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Back Pressure | 0.300 to 1.00 | MPa | |
| Screw Speed | 30 to 70 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 120°C/h |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MTEGRITY™ PS General Purpose GS220WC | M. Holland Company | PS (GPPS) | MTEGRITY™ PS General Purpose |
| Nylene® 7228 HS | Custom Resins Group | Nylon 6 | Nylene® |
| Andur 95 AP/Curene® 442 | Anderson Development Company | PUR-Ether/TDI | Andur |
| EZ-Spray® Plastic | Smooth-On, Inc | PUR, Unspecified | EZ-Spray® |
| Kumho EP HAB 8710NH | Korea Kumho Petrochemical Co., Ltd. | ABS+PBT | Kumho EP |