Andur 8-6 APSLM/Curene® 49
| Category: | PUR-Ester/TDI , Polyurethane (Polyester, TDI) |
| Manufacturer: | Anderson Development Company |
| Trademark: | Andur |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MfAeUd_Andur-8-6-APSLM-Curene-49.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Andur 8-6APSLM is a polyester based liquid, toluene diisocyanate terminated prepolymer designed to remain liquid at room temperature. Elastomers with a Shore A durometer hardness of 84-87 can be obtained when Andur 8-6APSLM is cured with Curene 442 [4,4'-methylene-bis (orthochloroaniline)]. Elastomers of lower hardness can be prepared by curing Andur 8-6APSLM with various polyols, combinations of polyols and Curene 442, other diamines, or through the use of plasticizers. |
| General Information | |
|---|---|
| Forms |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Durometer Hardness (Shore A) | 56 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% strain | 1.93 | MPa | ASTM D412 |
| 300% strain | 4.14 | MPa | ASTM D412 |
| Tensile Strength (Yield) | 35.9 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 460 | % | ASTM D412 |
| Compression Set | 2.0 | % | ASTM D395B |
| Bayshore Resilience | 18 | % | ASTM D2632 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Pot Life | 4.0 - 6.0 | min | |
| Demold Time | 30 | min | |
| Post Cure Time | |||
| 22°C | 72 | hr | |
| 99°C | 16 | hr |
| Additional Information |
|---|
| Die C Tear, ASTM D1004: 170 pliAverage Split Tear, ASTM D1938: 18 pliStoichiometry Curative Level: 95%Grams Curene 49 per 100 grams Andur 8 to 6 APSLM: 3.8Mix Temperature: Andur 8-6 APSLM: 190°F Curene 49: 235°F |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 113 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® S 35HRD 100 M NAT | Radici Plastics | Nylon 6 | Radilon® |
| Stat-Tech™ AS-1000 AS | PolyOne Corporation | ABS | Stat-Tech™ |
| WELLAMID Nylon 6600 GV 50 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 66 | WELLAMID Nylon |
| 4LAC® 10H20000 | 4Plas | ABS | 4LAC® |
| DIALAC® S359E | UMG ABS, Ltd. | ASA+PMMA | DIALAC® |