LEXAN™ HFD1810 resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Mf6fkV_LEXANHFD1810resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 40 MFR LEXAN High Flow Ductile Copolymer |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 40 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 250°C/1.2 kg | 7.00 | cm³/10min | ISO 1133 |
| 300°C/1.2 kg | 38.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 - 0.70 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.30 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.15 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2270 | MPa | ASTM D638 |
| -- | 2180 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 60.0 | MPa | ASTM D638 |
| Yield | 63.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 56.0 | MPa | ASTM D638 |
| Fracture | 56.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 5.5 | % | ASTM D638 |
| Yield | 6.0 | % | ISO 527-2/50 |
| Fracture 5 | 130 | % | ASTM D638 |
| Fracture | 97 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 6 | 2240 | MPa | ASTM D790 |
| -- 7 | 2180 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 91.0 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9 | ISO 179/1eA | ||
| -30°C | 13 | kJ/m² | ISO 179/1eA |
| 23°C | 64 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 10 | ISO 179/1eU | ||
| -30°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU | |
| Notched Izod Impact | |||
| -30°C | 110 | J/m | ASTM D256 |
| 0°C | 700 | J/m | ASTM D256 |
| 23°C | 730 | J/m | ASTM D256 |
| -30°C 11 | 11 | kJ/m² | ISO 180/1A |
| 23°C 12 | 58 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 13 | ISO 180/1U | ||
| -30°C | No Break | ISO 180/1U | |
| 23°C | No Break | ISO 180/1U | |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 56.0 | J | ASTM D3763 |
| -- | 95.0 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 121 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 110 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 14 | 115 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 135 | °C | ASTM D1525 15 |
| -- | 129 | °C | ISO 306/B50 |
| -- | 130 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 8.0E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 8.0E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| RTI Elec | 105 | °C | UL 746 |
| RTI Imp | 105 | °C | UL 746 |
| RTI | 105 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.300 mm | HB | UL 94 | |
| 1.00 mm | V-2 | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.582 | ASTM D542 | |
| Transmittance (2540 µm) | 88.0 | % | ASTM D1003 |
| Haze (2540 µm) | < 1.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 - 110 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 24 | hr | |
| Suggested Shot Size | 40 - 60 | % | |
| Rear Temperature | 238 - 282 | °C | |
| Middle Temperature | 249 - 293 | °C | |
| Front Temperature | 260 - 304 | °C | |
| Nozzle Temperature | 254 - 299 | °C | |
| Processing (Melt) Temp | 260 - 304 | °C | |
| Mold Temperature | 48.9 - 82.2 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 35 - 75 | rpm | |
| Vent Depth | 0.038 - 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*3 sp=62mm |
| 10 . | 80*10*3 sp=62mm |
| 11 . | 80*10*3 |
| 12 . | 80*10*3 |
| 13 . | 80*10*3 |
| 14 . | 80*10*4 mm |
| 15 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MORETEC™ 00138H | Prime Polymer Co., Ltd. | LLDPE | MORETEC™ |
| TIPPLEN® K 395 A | MOL Petrochemicals Co. Ltd. | PP Impact Copolymer | TIPPLEN® |
| WONDERLITE® PC-110 | CHI MEI CORPORATION | PC | WONDERLITE® |
| AKROMID® A3 GM 15/15 natural (1022) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| NHU-PPS 1150C | Zhejiang NHU Comp. Ltd. | PPS | NHU-PPS |