POLYFLAM® RIPP 5000 CC
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | A. Schulman Europe |
| Trademark: | POLYFLAM® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Mef96V_POLYFLAMRIPP5000CC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Unfilled flame-retardant PP-Copolymer for extrusion and cable coating with continius use temperature -40°C to 125°C |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.15 | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 3.50 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 49 | DIN 53505 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 500 | MPa | ISO 527-2/1A/1 |
| Tensile Stress | ISO 527-2/1A/50 | ||
| Yield | 11.0 | MPa | ISO 527-2/1A/50 |
| Fracture | 15.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 27 | % | ISO 527-2/1A/50 |
| Nominal Tensile Strain at Break | 400 | % | ISO 527-2/1A/50 |
| Flexural Modulus 1 | 650 | MPa | ISO 178 |
| Flexural Stress 2 | ISO 178 | ||
| 6.6% strain | 13.0 | MPa | ISO 178 |
| 3.5% strain | 12.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 4.0 | kJ/m² | ISO 179/1eA |
| 23°C | 55 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 55.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 45.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 83.0 | °C | ISO 306/A50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 0.8 mm | V-2 | IEC 60695-11-10, -20 | |
| 1.6 mm | V-2 | IEC 60695-11-10, -20 | |
| 3.2 mm | V-2 | IEC 60695-11-10, -20 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 0.75 mm | 960 | °C | IEC 60695-2-12 |
| 1.5 mm | 960 | °C | IEC 60695-2-12 |
| 3.0 mm | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.75 mm | 675 | °C | IEC 60695-2-13 |
| 1.5 mm | 675 | °C | IEC 60695-2-13 |
| 3.0 mm | 675 | °C | IEC 60695-2-13 |
| Oxygen Index | 27 | % | ISO 4589-2 |
| Additional Information |
|---|
| 1.) Not for use in food contact applications2.) Not for use in medical or pharmaceutical applications |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 900 P-1720 | RTP Company | PSU | RTP |
| Verolloy B5536 | PlastxWorld Inc. | ABS+PBT | Verolloy |
| Nanguang TPU S-85AX | Fujian Nanguang Light Industry Co., Ltd. | TPU, Unspecified | Nanguang TPU |
| FHR Polypropylene P4G4B-036 | Flint Hills Resources, LP | PP Homopolymer | FHR Polypropylene |
| Fainplast PVC RKS 430/W-OM | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |