GELOY™ XTPMFR10 resin
| Category: | ASA+PC , Acrylonitrile Styrene Acrylate + PC |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | GELOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MeEtzi_GELOYXTPMFR10resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Improved ASA/PC blend for high flow, 1.0mm V0 applications. Improved UV performance aesthetically and physically compared to alternatives. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.18 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (260°C/2.16 kg) | 30.0 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2680 | MPa | ASTM D638 |
| -- | 2680 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 60.0 | MPa | ASTM D638 |
| Yield 3 | 65.0 | MPa | ASTM D638 |
| Yield | 61.0 | MPa | ISO 527-2/5 |
| Yield | 66.0 | MPa | ISO 527-2/50 |
| Fracture 4 | 49.0 | MPa | ASTM D638 |
| Fracture 5 | 47.0 | MPa | ASTM D638 |
| Fracture | 46.0 | MPa | ISO 527-2/5 |
| Fracture | 47.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 6 | 4.0 | % | ASTM D638 |
| Yield 7 | 4.0 | % | ASTM D638 |
| Yield | 4.0 | % | ISO 527-2/5, ISO 527-2/50 |
| Fracture 8 | 58 | % | ASTM D638 |
| Fracture 9 | 31 | % | ASTM D638 |
| Fracture | 50 | % | ISO 527-2/5 |
| Fracture | 21 | % | ISO 527-2/50 |
| Flexural Modulus 10 | 2730 | MPa | ISO 178 |
| Flexural Stress | 97.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 11(23°C) | 13 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 90 | J/m | ASTM D256 |
| 23°C | 330 | J/m | ASTM D256 |
| 0°C 12 | 12 | kJ/m² | ISO 180/1A |
| 23°C 13 | 13 | kJ/m² | ISO 180/1A |
| Multi-Axial Instrumented Impact Energy | 85.0 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 14 | |||
| 0.45 MPa, unannealed, 64.0mm span | 90.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 64.0mm span | 81.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 96.0 | °C | ISO 306/B50 |
| -- | 98.0 | °C | ISO 306/B120 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : -40 to 40°C | 6.3E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 6.3E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.0 mm, Testing by SABIC) | V-0 | UL 94 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (260°C, 1500 sec^-1) | 105 | Pa·s | ISO 11443 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 - 90 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 60 - 80 | °C | |
| Rear Temperature | 200 - 230 | °C | |
| Middle Temperature | 220 - 260 | °C | |
| Front Temperature | 230 - 270 | °C | |
| Nozzle Temperature | 220 - 260 | °C | |
| Processing (Melt) Temp | 230 - 270 | °C | |
| Mold Temperature | 50 - 70 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 5.0 mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | Type 1, 5.0 mm/min |
| 7 . | Type 1, 50mm/min |
| 8 . | Type 1, 5.0 mm/min |
| 9 . | Type 1, 50mm/min |
| 10 . | 2.0 mm/min |
| 11 . | 80*10*4 sp=62mm |
| 12 . | 80*10*4 |
| 13 . | 80*10*4 |
| 14 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 600 FR AW | RTP Company | ABS | RTP |
| Chemical Resources BPP3000 | Chemical Resources, Inc. | PP Impact Copolymer | Chemical Resources |
| Hostacom EKC 265N G71350 | LyondellBasell Industries | PP, Unspecified | Hostacom |
| POLYfill PPHC T20050 | Polykemi AB | PP, Unspecified | POLYfill |
| TECHNYL® C 236SI V30 NATURAL | Solvay Engineering Plastics | Nylon 6 | TECHNYL® |