Hostalen PP H5416 K
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostalen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Mdg0pm_Hostalen-PP-H5416-K.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Hostalen PP H5416 K is a natural nucleated polypropylene random copolymer. The product has a high heat- and extremely high extraction stability. It is not intended for medical and pharmaceutical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183, ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238, ISO 1133 | ||
| 190°C/5.0 kg | 0.50 | g/10 min | |
| 230°C/2.16 kg | 0.30 | g/10 min | |
| 230°C/5.0 kg | 1.3 | g/10 min |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 800 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 26.5 | MPa | ASTM D638 |
| Yield, 23°C | 24.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield | 10 | % | ASTM D638 |
| Yield, 23°C | 10 | % | ISO 527-2/50 |
| Flexural Modulus (23°C) | 834 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -20°C | 45 | kJ/m² | |
| 0°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact (23°C) | 230 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 83.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 65.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | |||
| -- | 123 | °C | ASTM D1525 |
| -- | 125 | °C | ISO 306/A50 |
| Melting Temperature 1 | 141 | °C | ISO 11357-3 |
| CLTE - Flow (23 to 80°C) | 1.5E-4 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.24 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+14 | ohms | ASTM D257, IEC 60093 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 200 to 280 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 200 to 230 | °C |
| Note Message | |
|---|---|
| 1 . | 10°C/min, 2nd heating |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shanghai Potomer SG4 | Shanghai Potomer International Trade Co., Ltd. | PVC, Flexible | Shanghai Potomer |
| Stylac™ IM15 | Asahi Kasei Chemicals Corporation | ABS | Stylac™ |
| Karina IVORY PVC COMPOUND -E 90900-35/1-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| ISOPAK® 525 | Great Eastern Resins Industrial Co Ltd (GRECO) | ABS | ISOPAK® |
| Durethan® BG 30 X XF 000000 | LANXESS GmbH | Nylon 6 | Durethan® |