VICTREX® PEEK 90HMF40

Category:	PEEK , Polyetheretherketone
Manufacturer:	Victrex plc
Trademark:	VICTREX® PEEK
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	MdcXSh_VICTREX-PEEK-90HMF40.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

High performance thermoplastic material, 40% carbon fibre reinforced PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection moulding, easy flow, colour black.

Complex geometries with thinner cross sections or longer flow length where superior strength in a static or dynamic system is required. Excellent wear resistance, low coefficient of friction, low coefficient of thermal expansion. Chemically resistant to aggressive environments.

General Information
Filler / Reinforcement	Carbon fiber reinforced material, 40% filler by weight
Features	Semicrystallization Low friction coefficient High strength Good liquidity Good chemical resistance Good wear resistance
Appearance	Black
Forms	Particles
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Density ¹	1.45	g/cm³	ISO 1183
Spiral Flow	10.0	cm	Internal method
Molding Shrinkage ²			ISO 294-4
Vertical flow direction	0.40	%	ISO 294-4
Flow direction	0.0	%	ISO 294-4
Water Absorption			ISO 62
23°C, 24 hr, 3.20 mm	0.030	%	ISO 62
Saturated, 23°C, 3.20mm	0.30	%	ISO 62

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D)	89		ISO 868

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C)	45000	MPa	ISO 527-2
Tensile Stress			ISO 527-2
Fracture, 23°C	330	MPa	ISO 527-2
Fracture, 120°C	220	MPa	ISO 527-2
Fracture, 180°C	145	MPa	ISO 527-2
Fracture, 275°C	85.0	MPa	ISO 527-2
Tensile Strain (Break, 23°C)	1.2	%	ISO 527-2
Flexural Modulus (23°C)	37000	MPa	ISO 178
Flexural Stress			ISO 178
23°C	480	MPa	ISO 178
120°C	350	MPa	ISO 178
180°C	220	MPa	ISO 178
275°C	120	MPa	ISO 178
Compressive Stress			ISO 604
23°C	310	MPa	ISO 604
120°C	250	MPa	ISO 604
200°C	120	MPa	ISO 604

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	8.0	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	60	kJ/m²	ISO 179/1U
Notched Izod Impact (23°C)	11	kJ/m²	ISO 180/A
Unnotched Izod Impact Strength (23°C)	60	kJ/m²	ISO 180

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed)	349	°C	ISO 75-2/Ae
Glass Transition Temperature	143	°C	ISO 11357-2
Melting Temperature	343	°C	ISO 11357-3
Linear thermal expansion coefficient			ISO 11359-2
Flow : > 143°C	1.0E-6	cm/cm/°C	ISO 11359-2
Flow : < 143°C	3.0E-6	cm/cm/°C	ISO 11359-2
Lateral : < 143°C	3.5E-5	cm/cm/°C	ISO 11359-2
Lateral : > 143°C	8.0E-5	cm/cm/°C	ISO 11359-2
Specific Heat (23°C)	1800	J/kg/°C	DSC
Thermal Conductivity (23°C)	2.0	W/m/K	ISO 22007-4

Electrical	Nominal Value	Unit	Test Method
Volume Resistivity ³(23°C)	1.0E+5	ohms·cm	ASTM D4496

Fill Analysis	Nominal Value	Unit	Test Method
Melt Viscosity (400°C)	330	Pa·s	ISO 11443

Injection	Nominal Value	Unit
Drying Temperature	120 - 150	°C
Drying Time	3.0 - 5.0	hr
Hopper Temperature	< 100	°C
Rear Temperature	365	°C
Middle Temperature	370 - 375	°C
Front Temperature	380	°C
Nozzle Temperature	385	°C
Mold Temperature	190 - 200	°C

Injection instructions
Runner: Die / nozzle >3mm, manifold >3.5mmGate: >2mm or 0.5 x part thickness

Note Message
1 .	Crystalline
2 .	380°C nozzle, 190°C tool
3 .	1V

Resin Grade	Manufacturer	Category	Trademark
Marlex® 9346	Chevron Phillips Chemical Company LLC	HDPE	Marlex®
NuSil FS-3602	NuSil Technology	Silicone	NuSil
Hiprolon® 70 MNNHL G30	Arkema	Nylon 610	Hiprolon®
Plaslube® PA6/6 LCX 04	Techmer Engineered Solutions	Nylon 66	Plaslube®
Mediprene® 880135	ELASTO	SEBS	Mediprene®