EVAL™ M100B
| Category: | EVOH , Ethylene Vinyl Alcohol |
| Manufacturer: | EVAL Europe nv |
| Trademark: | EVAL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Md4TVM_EVAL-M100B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EVAL™ M100B is an Ethylene Vinyl Alcohol (EVOH) product. It is available in Europe. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.22 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 210°C/2.16 kg | 2.2 | g/10 min | |
| 230°C/2.16 kg | 3.8 | g/10 min | |
| 250°C/2.16 kg | 4.9 | g/10 min | |
| Ethylene Content | 24.0 | mol% | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 97 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3200 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 45.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 14 | % | ISO 527-2 |
| Flexural Modulus | 4800 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Permeability 1 | ISO 14663-2 | ||
| 20°C, 0% RH | 1.0E-3 | cm³·mm/m²/atm/24 hr | |
| 20°C, 100% RH | 0.042 | cm³·mm/m²/atm/24 hr | |
| 20°C, 35% RH | 1.0E-3 | cm³·mm/m²/atm/24 hr | |
| 20°C, 65% RH | 2.0E-3 | cm³·mm/m²/atm/24 hr | |
| 20°C, 85% RH | 0.016 | cm³·mm/m²/atm/24 hr | |
| Water Vapor Transmission Rate 2 | 3.4 | g·mm/m²/atm/24 hr | ASTM E96 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -- | 2.0 | kJ/m² | |
| -40°C | 3.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 60.0 | °C | ISO 11357-2 |
| Vicat Softening Temperature | 186 | °C | ISO 306 |
| Melting Temperature | 195 | °C | ISO 11357-3 |
| Peak Crystallization Temperature | 168 | °C | ISO 11357-3 |
| Note Message | |
|---|---|
| 1 . | Annex C |
| 2 . | Procedure E |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MIDILENA I LDPE B21/2 | ROMPETROL PETROCHEMICALS S.R.L. | LDPE | MIDILENA I |
| SCHULAFORM® 9 A GF 20 | A. Schulman Europe | Acetal (POM) Copolymer | SCHULAFORM® |
| ALAMID® 6 GF 25 HV SCHWARZ-9957 | LEIS Polytechnik - polymere Werkstoffe GmbH | Nylon 6 | ALAMID® |
| AMPLIFY™ GR 380 | The Dow Chemical Company | MAH-g | AMPLIFY™ GR |
| DELPET™ 80NR | Asahi Kasei Chemicals Corporation | Acrylic (PMMA) | DELPET™ |