Amodel® LF-1630 L NT-7 is 30% long carbon fiber reinforced, easy-flowing PPA which can be processed on most injection molding machines. This material achieves extremely high mechanical and thermal properties, in combination with ease of processing and fast cycle times. It exhibits high strength, stiffness and impact strength at high temperatures; excellent creep and fatigue resistance; isotropic mechanical properties and reduced isotropic shrinkage; high shear strength and high burst pressure; and an excellent surface finish.

General Information
Filler / Reinforcement	Long carbon fiber, 30% filler by weight
Features	Low CLTE Low warpage Rigidity, high Rigidity, high High tensile strength Insulation Impact resistance, high Good creep resistance Fatigue resistance Hot water formability
Uses	Gear Aircraft applications Application in Automobile Field Car dashboard
Appearance	Natural color
Forms	Particle

Physical	Nominal Value	Unit	Test Method
Density	1.30	g/cm³	ISO 1183
shrinkage- Flow ¹	0.25	%	Internal method
Water Absorption (Equilibrium, 23°C, 50% RH)	0.80	%	ISO 62

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C)	26000	MPa	ISO 527-2
Tensile Stress (Break, 23°C)	320	MPa	ISO 527-2
Tensile Strain (Break)	1.5	%	ISO 527-2
Flexural Modulus (23°C)	24500	MPa	ISO 178
Flexural Stress (23°C)	440	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	12	kJ/m²	ISO 179
Charpy Unnotched Impact Strength (23°C)	55	kJ/m²	ISO 179

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	300	°C	ISO 75-2/B
1.8 MPa, not annealed	285	°C	ISO 75-2/A

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	100	ohms/sq	ASTM D257

Injection	Nominal Value	Unit
Drying Temperature	120	°C
Drying Time	4.0	hr
Suggested Max Moisture	0.080	%
Suggested Max Regrind	20	%
Rear Temperature	320 - 340	°C
Middle Temperature	320 - 335	°C
Front Temperature	320 - 335	°C
Nozzle Temperature	325 - 340	°C
Processing (Melt) Temp	< 340	°C
Mold Temperature	135 - 165	°C

Injection instructions
Pre-Drying -- Since polyamides are hygroscopic materials as well as sensitive to moisture during processing, this product should always be pre-dried.Regrind -- Regrind of highly filled thermoplastic materials, such as this material, should only be recycled with special care. The regrind content must never exceed 20% and only regrind of optimum quality should be used. In any case, part properties should be checked.

Injection instructions

Pre-Drying -- Since polyamides are hygroscopic materials as well as sensitive to moisture during processing, this product should always be pre-dried.Regrind -- Regrind of highly filled thermoplastic materials, such as this material, should only be recycled with special care. The regrind content must never exceed 20% and only regrind of optimum quality should be used. In any case, part properties should be checked.

Note Message
1 .	Tested in accordance with S.O.P. methods

Category:	PPA , Polyphthalamide
Manufacturer:	Solvay Specialty Polymers
Trademark:	Amodel®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	McqPGH_AmodelLF1630LNT7.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Pyramid™ PAEK KD210SG	Polymics, Ltd.	PAEK	Pyramid™ PAEK
Sumikon® FM-MK124	Sumitomo Bakelite Co., Ltd.	PPS	Sumikon®
ASTALAC™ ABS 2147	Marplex Australia Pty. Ltd.	ABS	ASTALAC™
Hanwha Total PP BI451	HANWHA TOTAL PETROCHEMICALS Co., Ltd.	PP, High Crystal	Hanwha Total PP
Deprene 101-80	Shanghai Lin Gen Rubber Materials Co., Ltd.	PP+EPDM	Deprene