Haysite Plastics HST-II
| Category: | Polyester, TS , Thermoset Polyester |
| Manufacturer: | Haysite Reinforced Plastics |
| Trademark: | Haysite Plastics |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Mclpcb_Haysite-Plastics-HST-II.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| UL, Inc. has granted HST-II the highest thermal recognition ever achieved by any glass polyester laminate (U.L. File No. E81893). HST-II has a 220° C/210° C rating for 1/8" thick and heavier, and a 210° C/210° C rating for 1/32" thick up to 1/8" thick. HST-II is a high temperature polyester laminate that exhibits excellent retention of electrical and mechanical properties at elevated temperatures. Applications for HST-II can be found in high voltage transformers, D.C. motors and elsewhere when materials with high thermal indices are required. Available thicknesses - .031" - 2.00". Standard color - Brown. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.62 | g/cm³ | ASTM D792 |
| Water Absorption (Equilibrium) | 0.030 | % | ASTM D229 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Barcol Hardness | 52 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 89.6 | MPa | ASTM D638 |
| Flexural Modulus | 11700 | MPa | ASTM D790 |
| Flexural Strength | 172 | MPa | ASTM D790 |
| Compressive Strength | 228 | MPa | ASTM D695 |
| Shear Strength | 96.5 | MPa | ASTM D732 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 540 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CLTE - Flow | 2.9E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (1.59 mm, Oil) | 16 | kV/mm | ASTM D149 |
| Dielectric Constant (60 Hz) | 4.20 | ASTM D150 | |
| Dissipation Factor (60 Hz) | 0.010 | ASTM D150 | |
| Arc Resistance | 150 | sec | ASTM D495 |
| Dielectric Strength - Step-By-Step In Oil 1 | 62000 | V | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Resistance | ASTM D229 | ||
| Burning Time | 4.3 | min | |
| Ignition Time | 1.3 | min |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Bond Strength (1.27 cm) | 9.65 | MPa | ASTM D229 |
| Temperature Rating | 220 | °C |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | Parallel |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® A 303 NATURAL FA | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| Spartech Polycom PP5140F1 | Spartech Polycom | PP, Unspecified | Spartech |
| Sylvin 2911-55 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Mafill® CR CT 5344 | Ravago Group | PP Copolymer | Mafill® |
| LNP™ LUBRICOMP™ RFP36 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |