Adstif HA612M
| Category: | PP, High Crystal , High Crystallinity Polypropylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Adstif |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | McNE2g_Adstif-HA612M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Adstif HA612M is a high crystallinity polypropylene homopolymer with an extremely high stiffness, good transparency and outstanding high temperature performances. It is especially designed for cast film applications where high rigidity, transparency and very good thermal characteristics are required. Adstif HA612M is particularly recommended for the production of coex film for Twist Wrapping on high speed packaging lines. Other applications include flowers and textile packaging, sterilizable and pasteurizable food packaging. Adstif HA612M does not contain neither slip nor antiblocking agents and is suitable for metallisable films. It is Calcium Stearate free. For regulatory information please refer to Adstif HA612M Product Stewardship Bulletin (PSB). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 7.0 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 72 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1900 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 38.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 7.0 | % | |
| Break | 20 | % |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Secant Modulus - MD 1(50 µm, Cast Film) | 900 | MPa | ASTM D882 |
| Tensile Strength - MD 2 | ASTM D882 | ||
| Yield, 50 µm, Cast Film | 22.0 | MPa | |
| Break, 50 µm, Cast Film | 37.0 | MPa | |
| Tensile Elongation - MD 3 | ASTM D882 | ||
| Yield, 50 µm, Cast Film | 7.0 | % | |
| Break, Cast Film | 860 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 106 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 158 | °C | ISO 306/A50 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.0 µm, Cast Film) | 69 | ASTM D2457 | |
| Haze (50.0 µm, Cast Film) | 5.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 25 mm/min |
| 2 . | 500 mm/min |
| 3 . | 500 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AKROMID® B3 GK 30 black (1827) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| Fluon® PFA P-65P | Asahi Glass Co., Ltd. | PFA | Fluon® |
| GAPEX® RPP20EU80BK | Ferro Corporation | PP, Unspecified | GAPEX® |
| HiFill® PC/PBT IM 5720 LE | Techmer Engineered Solutions | PC+PBT | HiFill® |
| NEOFLON™ NP-30 | DAIKIN AMERICA, INC. | FEP | NEOFLON™ |