Amilan® CM3006G-45
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Toray Resin Company |
| Trademark: | Amilan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MbskMp_Amilan-CM3006G-45.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Amilan® CM3006G-45 is a Polyamide 66 (Nylon 66) product filled with 45% glass fiber. It is available in Asia Pacific, Europe, or North America. Primary characteristic: heat resistant. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Part Marking Code |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.50 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | |||
| Across Flow : 3.00 mm 1 | 0.50 to 0.80 | -- | % | |
| Flow : 3.00 mm 2 | 0.20 to 0.40 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr | 0.40 | -- | % | |
| Saturation, 23°C | 4.8 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness | ISO 2039-2 | |||
| M-Scale, 23°C | 103 | -- | ||
| R-Scale, 23°C | 121 | -- |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Stress | ISO 527-2 | |||
| -40°C | 280 | 250 | MPa | |
| 23°C | 220 | 165 | MPa | |
| 80°C | 140 | 115 | MPa | |
| Tensile Strain | ISO 527-2 | |||
| Break, -40°C | 2.5 | -- | % | |
| Break, 23°C | 3.0 | -- | % | |
| Break, 80°C | 5.5 | -- | % | |
| Flexural Modulus | ISO 178 | |||
| -40°C | 15500 | 14400 | MPa | |
| 23°C | 13800 | 11000 | MPa | |
| 80°C | 8600 | 7300 | MPa | |
| Flexural Stress | ISO 178 | |||
| -40°C | 380 | 350 | MPa | |
| 23°C | 345 | 295 | MPa | |
| 80°C | 230 | 195 | MPa | |
| Compressive Stress | ISO 604 | |||
| -40°C | 265 | -- | MPa | |
| 23°C | 195 | -- | MPa | |
| 80°C | 120 | -- | MPa | |
| Shear Strength (23°C) | 105 | -- | MPa | ASTM D732 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -40°C | 12 | 12 | kJ/m² | |
| 23°C | 15 | 17 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -40°C | 85 | 90 | kJ/m² | |
| 23°C | 90 | 100 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 263 | -- | °C | ISO 75-2/B |
| Melting Temperature | 265 | -- | °C | DSC |
| CLTE - Flow | 2.0E-5 to 3.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Specific Heat | 1500 | -- | J/kg/°C | |
| Thermal Conductivity | 0.42 | -- | W/m/K |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | 1.0E+12 to 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 19 | -- | kV/mm | IEC 60243-1 |
| Dielectric Constant 3 | IEC 60250 | |||
| 23°C, 50 Hz | 4.70 | -- | ||
| 23°C, 1 kHz | 4.50 | -- | ||
| 23°C, 1 MHz | 4.10 | -- | ||
| Dissipation Factor 4 | IEC 60250 | |||
| 23°C, 50 Hz | 0.020 | -- | ||
| 23°C, 1 kHz | 0.020 | -- | ||
| 23°C, 1 MHz | 0.020 | -- |
| Note Message | |
|---|---|
| 1 . | 80x80x3 |
| 2 . | 80x80x3mm |
| 3 . | 60% RH |
| 4 . | 60% RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 178 HI | RTP Company | PP Copolymer | RTP |
| RTP 1003 UV | RTP Company | PBT | RTP |
| DENKA EVA TEX NA500 | Denka Company Limited | EVA | DENKA EVA TEX |
| Sylvin 6930X06 Grey 9610 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| RONFALIN® ABS 1353 A | A. Schulman Europe | ABS | RONFALIN® |