PROTEQ™ C2K30
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | PROTEQ™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MbCpgE_PROTEQ-C2K30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PROTEQ™ C2K30 is low melt flow, high impact and flame retardant grade of Polypropylene copolymer which meets the stringent UL94 V-2 and AS/NZS 60695.2.12 (IEC 60695-2-12) flammability tests. PROTEQ™ C2K30 has also been successfully validated against the requirements of AS1530.2-1993 (Flammability of Materials) in a 1.2 mm thick extruded strip. C2K30 is designed for profile extrusion and selective moulding applications requiring a tough material with a balance of rigidity, flame retardancy and processability. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.960 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 1.4 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore D | 71 | ||
| Shore D, 15 sec | 68 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.20 mm) | 26.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | > 300 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 1250 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 32.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 280 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | > 750 | J/m | ASTM D256 |
| Gardner Impact (3.20 mm) | 40.0 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 3.20 mm) | 78.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 148 | °C | ASTM D1525 5 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | V-2 | UL 94 | |
| Glow Wire Ignition Temperature (3.00 mm) | 960 | °C | AS/NZS 60695 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 to 90.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Cylinder Zone 1 Temp. | 150 to 180 | °C | |
| Cylinder Zone 2 Temp. | 160 to 190 | °C | |
| Cylinder Zone 3 Temp. | 170 to 200 | °C | |
| Cylinder Zone 4 Temp. | 170 to 200 | °C | |
| Cylinder Zone 5 Temp. | 180 to 210 | °C | |
| Melt Temperature | 190 to 220 | °C | |
| Die Temperature | 180 to 210 | °C | |
| Take-Off Roll | 70.0 to 105 | °C | |
| Back Pressure | 10.0 to 25.0 | MPa |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PureTherm® ESD 1500 | Tekni-Films, a div of Tekni-Plex | Film, PVC | PureTherm® |
| Xuchuan XCA-RS45A | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Axiall PVC 22951 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Kpren CM235 | Shandong Xuye New Materials Co., Ltd. | CM | Kpren |
| Hostacom G1 H01 | LyondellBasell Industries | PP Homopolymer | Hostacom |