ULTEM™ 1000RV resin
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Mar7Dh_ULTEM-1000RV-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Standard flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing; color dependant, see UL Yellow Card. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.27 | g/cm³ | ASTM D792 |
| -- | 1.25 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (337°C/6.6 kg) | 9.7 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (220°C/5.0 kg) | 13.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 1.3 | % | |
| Equilibrium, 23°C, 50% RH | 0.70 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3590 | MPa | ASTM D638 |
| -- | 3200 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 110 | MPa | ASTM D638 |
| Yield | 105 | MPa | ISO 527-2/5 |
| Break 3 | 90.0 | MPa | ASTM D638 |
| Break | 85.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 7.0 | % | ASTM D638 |
| Yield | 6.0 | % | ISO 527-2/5 |
| Break 5 | 60 | % | ASTM D638 |
| Break | 60 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 3440 | MPa | ASTM D790 |
| -- 7 | 3300 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 160 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 173 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 4.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 55 | J/m | ASTM D256 |
| 23°C | 53 | J/m | ASTM D256 |
| -30°C 10 | 6.0 | kJ/m² | ISO 180/1A |
| 23°C 11 | 6.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C) | 1300 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 6.40 mm | 201 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 215 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 219 | °C | ASTM D1525 13 |
| -- | 215 | °C | ISO 306/B50 |
| -- | 211 | °C | ISO 306/B120 |
| CLTE | |||
| Flow : -20 to 150°C | 5.6E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 5.0E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -20 to 150°C | 5.4E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 5.0E-5 | cm/cm/°C | ISO 11359-2 |
| RTI Elec | 170 | °C | UL 746 |
| RTI Imp | 170 | °C | UL 746 |
| RTI Str | 170 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength | ASTM D149 | ||
| 1.60 mm, in Air | 33 | kV/mm | |
| 1.60 mm, in Oil | 28 | kV/mm | |
| Dielectric Constant (1 kHz) | 3.15 | ASTM D150 | |
| Dissipation Factor | ASTM D150 | ||
| 1 kHz | 1.3E-3 | ||
| 2.45 GHz | 2.5E-3 | ||
| Arc Resistance 14 | PLC 5 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 4 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 3 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 2 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 1 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.400 mm | V-2 | ||
| 0.750 mm | V-1 V-0 | ||
| 3.00 mm | 5VA | ||
| Oxygen Index | 47 | % | ASTM D2863 |
| NBS Smoke Density - Flaming, Ds, 4 min | 0.700 | ASTM E662 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Drying Time, Maximum | 24 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 332 to 399 | °C | |
| Middle Temperature | 338 to 399 | °C | |
| Front Temperature | 343 to 399 | °C | |
| Nozzle Temperature | 343 to 399 | °C | |
| Processing (Melt) Temp | 349 to 399 | °C | |
| Mold Temperature | 135 to 163 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | Rate B (120°C/h), Loading 2 (50 N) |
| 14 . | Tungsten Electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sunny® PA6 EB230 | Guangdong Shunde Shunyan New Material Co., Ltd. | Nylon 6 | Sunny® |
| Sylvin 9067F4 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| MAJORIS FN080 | AD majoris | PP Copolymer | MAJORIS |
| OmniCarb™ PC GR30 | OMNI Plastics, LLC | PC | OmniCarb™ |
| Kinta FR3600B | Kinta Technology (Hong Kong) Co., Ltd. | ABS | Kinta |