Nypol® PA B3 T10 TZ PRTA011 NT382
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Nypol® PA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MaIgPg_Nypol-PA-B3-T10-TZ-PRTA011-NT382.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6 in black color with 10% of mineral reinforced tenacious. Good set of thermal properties, lubricated, electrical and mechanical. Ideal for injection molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.80 | % | ASTM D955 |
| Water Absorption (Equilibrium) | 0.15 | % | ASTM D570 |
| Ash Content | 8.0 to 12 | % | ASTM D2584 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 90.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 8.0 | % | ASTM D638 |
| Flexural Modulus | 4000 | MPa | ASTM D790 |
| Flexural Strength | 90.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 50 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 200 | °C | ASTM D648 |
| Melting Temperature | 210 to 225 | °C | ASTM D2117 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pyramid™ PEEK KD2000-J02 | Polymics, Ltd. | PEEK | Pyramid™ PEEK |
| Aplax P2620GN | Ginar Technology Co., LTD. | PP, Unspecified | Aplax |
| KOPA® KN135HB40BL | Kolon Plastics, Inc. | Nylon 6 | KOPA® |
| Leona™ 1402G | Asahi Kasei Chemicals Corporation | Nylon 66 | Leona™ |
| Stat-Tech™ PC-091104 | PolyOne Corporation | PC | Stat-Tech™ |