VALOX™ 420 resin Datasheet,PBT,SABIC Innovative Plastics-SHANGHAI SUSHENG

Message
30% GR, excellent strength, stiffness and dimensional stability. High heat resistance. Appliance handles, spotlights, electric motors, connectors.

General Information
Filler / Reinforcement	Glass Fiber, 30% Filler by Weight
Features	Good Dimensional Stability Good Stiffness Good Strength High Heat Resistance
Uses	Appliance Components Connectors Handles
Processing Method	Injection Molding
Multi-Point Data	Coefficient of Thermal Expansion vs. Temperature (ASTM E831) Elastic Modulus vs Temperature (ASTM D4065) Flexural DMA (ASTM D4065) Instrumented Impact (Energy) (ASTM D3763) Instrumented Impact (Load) (ASTM D3763) Pressure-Volume-Temperature (PVT - Zoller Method) Shear DMA (ASTM D4065) Specific Heat vs. Temperature (ASTM D3417) Tensile Creep (ASTM D2990) Tensile Fatigue Tensile Stress vs. Strain (ASTM D638) Thermal Conductivity vs. Temperature (ASTM E1530) Viscosity vs. Shear Rate (ASTM D3835)

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.53	g/cm³	ASTM D792
Specific Volume	0.660	cm³/g	ASTM D792

Additional Information	Nominal Value	Unit	Test Method
Filler Content	30	%	ASTM D229

Physical	Nominal Value	Unit	Test Method
Melt Mass-Flow Rate (MFR) (250°C/2.16 kg)	17	g/10 min	ISO 1133
Melt Volume-Flow Rate (MVR) (250°C/2.16 kg)	13.0	cm³/10min	ISO 1133
Molding Shrinkage			Internal Method
Flow ¹	0.30 to 0.70	%
Flow ²	0.30 to 0.50	%
Flow ³	0.50 to 0.80	%
Flow : 3.20 mm	0.30 to 0.80	%
Across Flow ⁴	0.50 to 1.0	%
Across Flow ⁵	0.40 to 0.60	%
Across Flow ⁶	0.60 to 0.90	%
Across Flow : 3.20 mm	0.50 to 1.0	%
Water Absorption
24 hr	0.090	%	ASTM D570
Equilibrium, 23°C, 50% RH	0.080	%	ISO 62

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (R-Scale)	118		ASTM D785, ISO 2039-2
Ball Indentation Hardness (H 358/30)	122	MPa	ISO 2039-1

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus
-- ⁷	9300	MPa	ASTM D638
--	9300	MPa	ISO 527-2/1
Tensile Strength
Yield ⁸	120	MPa	ASTM D638
Yield	125	MPa	ISO 527-2/5
Break ⁹	120	MPa	ASTM D638
Break	125	MPa	ISO 527-2/5
Tensile Elongation
Yield ¹⁰	2.7	%	ASTM D638
Yield	2.0	%	ISO 527-2/5
Break ¹¹	2.7	%	ASTM D638
Break	2.0	%	ISO 527-2/5
Flexural Modulus
50.0 mm Span ¹²	7580	MPa	ASTM D790
-- ¹³	8500	MPa	ISO 178
Flexural Stress
--	195	MPa	ISO 178
Yield, 50.0 mm Span ¹⁴	195	MPa	ASTM D790
Break, 50.0 mm Span ¹⁵	190	MPa	ASTM D790
Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel)	19.0	mg	ASTM D1044

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength ¹⁶			ISO 179/1eA
-30°C	5.0	kJ/m²
23°C	5.0	kJ/m²
Charpy Unnotched Impact Strength ¹⁷			ISO 179/1eU
-30°C	45	kJ/m²
23°C	45	kJ/m²
Notched Izod Impact
-30°C	80	J/m	ASTM D256
23°C	85	J/m	ASTM D256
-30°C ¹⁸	7.0	kJ/m²	ISO 180/1A
23°C ¹⁹	8.0	kJ/m²	ISO 180/1A
Unnotched Izod Impact
23°C	800	J/m	ASTM D4812
-30°C ²⁰	45	kJ/m²	ISO 180/1U
23°C ²¹	45	kJ/m²	ISO 180/1U
Instrumented Dart Impact (23°C, Total Energy)	8.00	J	ASTM D3763

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load
0.45 MPa, Unannealed, 3.20 mm	220	°C	ASTM D648
0.45 MPa, Unannealed, 6.40 mm	216	°C	ASTM D648
0.45 MPa, Unannealed, 64.0 mm Span ²²	217	°C	ISO 75-2/Bf
1.8 MPa, Unannealed, 3.20 mm	203	°C	ASTM D648
1.8 MPa, Unannealed, 6.40 mm	207	°C	ASTM D648
1.8 MPa, Unannealed, 64.0 mm Span ²³	204	°C	ISO 75-2/Af
Vicat Softening Temperature
--	215	°C	ASTM D1525, ISO 306/B50, ISO 306/B120 ²⁴
--	223	°C	ISO 306/A50
Ball Pressure Test (125°C)	Pass		IEC 60695-10-2
CLTE
Flow : -40 to 40°C	2.5E-5	cm/cm/°C	ASTM E831, ISO 11359-2
Flow : 60 to 138°C	2.5E-5	cm/cm/°C	ASTM E831
Transverse : -40 to 40°C	1.2E-4	cm/cm/°C	ASTM E831, ISO 11359-2
Thermal Conductivity	0.19	W/m/K	ISO 8302
RTI Elec	140	°C	UL 746
RTI Imp	140	°C	UL 746
RTI Str	140	°C	UL 746

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	> 1.0E+15	ohms	IEC 60093
Volume Resistivity
--	> 3.2E+16	ohms·cm	ASTM D257
--	> 1.0E+15	ohms·cm	IEC 60093
Dielectric Strength
1.60 mm, in Oil	25	kV/mm	ASTM D149
3.20 mm, in Air	19	kV/mm	ASTM D149
0.800 mm, in Oil	28	kV/mm	IEC 60243-1
1.00 mm ²⁵	19	kV/mm	IEC 60243-1
1.60 mm, in Oil	24	kV/mm	IEC 60243-1
3.20 mm, in Oil	16	kV/mm	IEC 60243-1
Dielectric Constant
100 Hz	3.80		ASTM D150
1 MHz	3.70		ASTM D150
50 Hz	3.10		IEC 60250
60 Hz	3.10		IEC 60250
1 MHz	3.10		IEC 60250
Dissipation Factor
100 Hz	2.0E-3		ASTM D150
1 MHz	0.020		ASTM D150
50 Hz	1.0E-3		IEC 60250
60 Hz	1.0E-3		IEC 60250
100 Hz	1.0E-3		IEC 60250
1 MHz	0.010		IEC 60250
Arc Resistance ²⁶	PLC 5		ASTM D495
Comparative Tracking Index (CTI)	PLC 0		UL 746
Comparative Tracking Index	300	V	IEC 60112
High Voltage Arc Tracking Rate (HVTR)	PLC 1		UL 746

Flammability	Nominal Value	Unit	Test Method
Flame Rating (0.840 mm)	HB		UL 94
Glow Wire Flammability Index (1.00 mm)	750	°C	IEC 60695-2-12
Oxygen Index	19	%	ASTM D2863

Category:	PBT , Polybutylene Terephthalate
Manufacturer:	SABIC Innovative Plastics
Trademark:	VALOX™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	MZbg4i_VALOX-420-resin.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
RTP 1385 C TFE 15	RTP Company	PPS	RTP
Spartech Polycom PP6430 B9	Spartech Polycom	PP, Unspecified	Spartech
TPUCO® TPU-C85	Taiwan PU Corporation	TPU-Polyester	TPUCO®
Topolymer® 9210-503	Dongguan Top Polymer Enterprise	TPV	Topolymer®
MAJORIS DT360 - 8229	AD majoris	PP, Unspecified	MAJORIS