INEOS LDPE 23H430
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | INEOS Olefins & Polymers Europe |
| Trademark: | INEOS LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MZOp3E_INEOS-LDPE-23H430.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Applications 23H430 is suitable for a variety of general-purpose packaging films, liners, carrier bags and fine shrink film. It is also recommended for cross-linked foam as well as for blow-moulding applications. Benefits and Features 23H430 is an autoclave LDPE homopolymer. It offers the following properties:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.923 | g/cm³ | ISO 1183/D |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (Blown Film) | > 0.50 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Tensile Modulus - 1% Secant (50 µm, Blown Film) | 180 | MPa | ISO 1184 |
| Tensile Stress | ISO 1184 | ||
| MD : Yield, 50 µm, Blown Film | 11.0 | MPa | |
| TD : Yield, 50 µm, Blown Film | 12.0 | MPa | |
| MD : Break, 50 µm, Blown Film | 22.0 | MPa | |
| TD : Break, 50 µm, Blown Film | 20.0 | MPa | |
| Tensile Elongation | ISO 1184 | ||
| MD : Break, 50 µm, Blown Film | 250 | % | |
| TD : Break, 50 µm, Blown Film | 550 | % | |
| Dart Drop Impact (50 µm, Blown Film) | 140 | g | ASTM D1709A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 95.0 | °C | ISO 306/A |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.0 µm, Blown Film) | 55 | ASTM D2457 | |
| Haze (50.0 µm, Blown Film) | 10 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 160 to 185 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Promyde® B30 P2 HI | NUREL, S.A. | Nylon 6 | Promyde® |
| Spartech Polycom SC2-1230S | Spartech Polycom | PS (HIPS) | Spartech |
| TYNE® ABS CBE 75 | Tyne Plastics LLC. | ABS | TYNE® ABS |
| UBE Polyethylene J1019 | UBE America, Inc. | PE, Unspecified | UBE Polyethylene |
| Petrothene® NA443023 (Blown) | LyondellBasell Industries | LDPE | Petrothene® |