Order Products : sales@su-jiao.com
LNP™ LUBRICOMP™ DP0039EF compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MYDyT2_LNP-LUBRICOMP-DP0039EF-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP DP0039EF is a compound based on Polycarbonate resin containing Silicone, PTFE. Added features of this material include: Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound DP0039EF Product reorder name: DP0039EF |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.31 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/2.16 kg) | 18 | g/10 min | ASTM D1238 |
| Molding Shrinkage 1 | Internal Method | ||
| Flow | 0.68 | % | |
| Across Flow | 0.67 | % | |
| Water Absorption (Saturation, 23°C) | 0.050 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 2130 | MPa | ASTM D638 |
| -- | 2100 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 50.0 | MPa | ASTM D638, ISO 527-2 |
| Break | 40.0 | MPa | ASTM D638 |
| Break | 39.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 5.5 | % | ASTM D638, ISO 527-2 |
| Break | 15 | % | ASTM D638 |
| Break | 18 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2140 | MPa | ASTM D790 |
| -- | 2180 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 80.0 | MPa | ASTM D790 |
| -- | 82.2 | MPa | ISO 178 |
| Coefficient of Friction (vs. Itself - Dynamic) | 0.17 | ASTM D3702 Modified | |
| Wear Factor - Washer | 422 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 300 | J/m | ASTM D256 |
| 23°C 3 | 19 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 2000 | J/m | ASTM D4812 |
| 23°C 4 | 130 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 23.0 | J | ASTM D3763 |
| -- | 61.5 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 126 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 128 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 304 to 316 | °C | |
| Front Temperature | 310 to 321 | °C | |
| Processing (Melt) Temp | 299 to 316 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 1.5 to 3.2 mm |
| 2 . | 5.0 mm/min |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Menzolit® BMC 0200 | Menzolit Ltd (UK) | Polyester, TS | Menzolit® |
| SLOVALEN® PH 69 GF 40 TS | Plastcom | PP, Unspecified | SLOVALEN® |
| Sylvin 8880-70LG Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LUVOCOM® 20-8943 | Lehmann & Voss & Co. | PPA | LUVOCOM® |
| OTECH TPE OTE7030 - Power Jacket | OTECH Corporation | TPE | OTECH TPE |