Milastomer™ G750BS
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | Mitsui Chemicals America, Inc. |
| Trademark: | Milastomer™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MXsr4P_Milastomer-G750BS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Milastomer™G750BS is a thermoplastic vulcanized rubber (TPV) material,. This product is available in North America and is processed by injection molding. |
| General Information | |
|---|---|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.880 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.2 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ISO 48 | ||
| Shaw A | 78 | ISO 48 | |
| Shaw A, 5 seconds | 74 | ISO 48 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1(100% Strain) | 3.00 | MPa | ISO 37 |
| Tensile Stress 2(Break) | 5.80 | MPa | ISO 37 |
| Tensile Elongation 3(Break) | 450 | % | ISO 37 |
| Compression Set (70°C, 22 hr) | 42 | % | ISO 815 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -60.0 | °C | Internal method |
| Additional Information |
|---|
| All tests performed according to Mitsui methods. |
| Note Message | |
|---|---|
| 1 . | 500 mm/min |
| 2 . | 500 mm/min |
| 3 . | 500 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Siloxane Masterbatch MB50-320 | Multibase, A Dow Corning Company | Siloxane, UHMW | Siloxane Masterbatch |
| Spartech Polycom SCR1-5005 | Spartech Polycom | ABS | Spartech |
| MonoSol® M3030 | MonoSol, LLC | PVOH | MonoSol® |
| ALTECH® PA66 A 2015/109 GF15 GN1140-13 | ALBIS PLASTIC GmbH | Nylon 66 | ALTECH® PA66 |
| Extir® LN 2001 | Versalis S.p.A. | PS (EPS) | Extir® |