UmaPET HC
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Ester Industries Ltd. |
| Trademark: | UmaPET |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MXgfRG_UmaPET-HC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
KEY FEATURES
APPLICATIONS
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage | ASTM D1204 | ||
| Flow : 150°C, 30 min, 0.0230 mm | 2.5 | % | |
| Flow : 150°C, 30 min, 0.0360 mm | 2.5 | % | |
| Flow : 150°C, 30 min, 0.0500 mm | 2.0 | % | |
| Across Flow : 150°C, 30 min, 0.0230 mm | 0.40 | % | |
| Across Flow : 150°C, 30 min, 0.0360 mm | 0.40 | % | |
| Across Flow : 150°C, 30 min, 0.0500 mm | 0.40 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic 1 | 0.40 | ||
| vs. Itself - Dynamic 2 | 0.42 | ||
| vs. Itself - Dynamic 3 | 0.40 | ||
| vs. Itself - Static 4 | 0.48 | ||
| vs. Itself - Static 5 | 0.50 | ||
| vs. Itself - Static 6 | 0.50 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 23 36 50 | µm | |
| Film Thickness - Recommended / Available | 23, 36, 50 µm | ||
| Tensile Strength | ASTM D882 | ||
| MD : Break, 23 µm | 186 | MPa | |
| MD : Break, 36 µm | 177 | MPa | |
| MD : Break, 50 µm | 167 | MPa | |
| TD : Break, 23 µm | 206 | MPa | |
| TD : Break, 36 µm | 186 | MPa | |
| TD : Break, 50 µm | 177 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 23 µm | 100 | % | |
| MD : Break, 36 µm | 130 | % | |
| MD : Break, 50 µm | 140 | % | |
| TD : Break, 23 µm | 90 | % | |
| TD : Break, 36 µm | 120 | % | |
| TD : Break, 50 µm | 130 | % | |
| Yield | Internal Method | ||
| 23.0 µm | 31.0 | m²/kg | |
| 36.0 µm | 19.8 | m²/kg | |
| 50.0 µm | 14.1 | m²/kg |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Wetting Tension - Plain side | ASTM D2578 | ||
| 23.0 µm | 44 | dyne/cm | |
| 36.0 µm | 44 | dyne/cm | |
| 50.0 µm | 44 | dyne/cm |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance | ASTM D1003 | ||
| 23.0 µm | 90.0 | % | |
| 36.0 µm | 90.0 | % | |
| 50.0 µm | 90.0 | % | |
| Haze | ASTM D1003 | ||
| 23.0 µm | 1.6 | % | |
| 36.0 µm | 1.8 | % | |
| 50.0 µm | 2.0 | % |
| Note Message | |
|---|---|
| 1 . | 50 µm |
| 2 . | 36 µm |
| 3 . | 23 µm |
| 4 . | 23 µm |
| 5 . | 36 µm |
| 6 . | 50 µm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEXUS PE HDPE-1062 | Nexus Resin Group, LLC. | HDPE | NEXUS PE |
| Chemiton GA H2NA 85 | Franplast S.r.l. | SEBS | Chemiton |
| Karina BEIGE COLOR CONCENTRATE -E 08/244-RG-GE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LUVOCOM® 1-8181 | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |
| RTP 1199 A X 136859 B EG | RTP Company | PETG | RTP |