ALTECH® PS A 1000/500
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | ALBIS PLASTIC GmbH |
| Trademark: | ALTECH® PS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MXagCR_ALTECH-PS-A-1000-500.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ALTECH® PS A 1000/500 is a High Impact Polystyrene product. It can be processed by injection molding and is available in Asia Pacific, Europe, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.03 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (200°C/5.0 kg) | 14.0 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 88.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2200 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 25.0 | MPa | |
| -- | 25.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 1.0 | % | |
| Break | 11 | % | |
| Flexural Modulus | 2250 | MPa | ISO 178 |
| Flexural Stress | ISO 178 | ||
| -- | 40.0 | MPa | |
| 3.5% Strain | 39.0 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 6.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -- | 50 | kJ/m² | |
| -40°C | 25 | kJ/m² | |
| -20°C | 45 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 76.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 81.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.00 mm | 650 | °C | |
| 2.00 mm | 650 | °C | |
| 3.00 mm | 650 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| Circulation Dryer | 60.0 to 80.0 | °C | |
| Desiccant Dryer | 60.0 to 80.0 | °C | |
| Drying Time | |||
| Circulation Dryer | 2.0 to 3.0 | hr | |
| Desiccant Dryer | 2.0 to 3.0 | hr | |
| Processing (Melt) Temp | 180 to 260 | °C | |
| Mold Temperature | 10.0 to 70.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polypropylene Lumicene® MR 10MX0 | TOTAL Refining & Chemicals | PP Random Copolymer | TOTAL Polypropylene |
| DIC.PPS FZL-4033 | DIC Corporation | PPS | DIC.PPS |
| HANWHA EVA 1533 | Hanwha Chemical | EVA | HANWHA EVA |
| Petrotene® PP A3 G18 FR NTLA010 PH325 | Petropol Industry and Trade of Polymers LTDA | PP, Unspecified | Petrotene® PP |
| ARLEN™ E440NK | Mitsui Chemicals, Inc. | Nylon 6T | ARLEN™ |