EMERGE™ PC/ABS 7100
| Category: | PC+ABS , Advanced Resin |
| Manufacturer: | Trinseo |
| Trademark: | EMERGE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MXSWOf_EMERGE-PC-ABS-7100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EMERGE™ PC/ABS 7100 advanced resin exhibits a balance of properties between impact strength, heat resistance and processability. Its superior natural base color and lot-to-lot color consistency makes it ideally suited for producing very consistent colored parts. It has excellent flow and is ideal for injection molding in thin-wall applications, such as portable electronic devices. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.11 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 230°C/3.8 kg | 4.5 | g/10 min | |
| 260°C/5.0 kg | 25 | g/10 min | |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 3.20 mm, Injection Molded) | 112 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (3.20 mm, Injection Molded) | 2210 | MPa | ASTM D638 |
| Tensile Strength 1(Yield, 3.20 mm, Injection Molded) | 50.3 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield, 3.20 mm, Injection Molded | 4.0 | % | |
| Break, 3.20 mm, Injection Molded | 50 | % | |
| Flexural Modulus (3.20 mm, Injection Molded) | 2340 | MPa | ASTM D790 |
| Flexural Strength (3.20 mm, Injection Molded) | 80.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.20 mm, Injection Molded | 290 | J/m | |
| 23°C, 3.20 mm, Injection Molded | 480 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm, Injection Molded | 116 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm, Injection Molded | 95.0 | °C | |
| Vicat Softening Temperature | 133 | °C | ASTM D1525 2 |
| CLTE - Flow | 7.6E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating 3(1.00 mm) | HB | UL 94 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Drying Temperature |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Processing (Melt) Temp | 238 to 266 | °C | |
| Mold Temperature | 48.9 to 90.6 | °C |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | Rate B (120°C/h), Loading 1 (10 N) |
| 3 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Miflon® 3113 | Jiangsu Meilan Chemical Co., Ltd. | PTFE | Miflon® |
| Milastomer™ C800BM | Mitsui Chemicals America, Inc. | TPV | Milastomer™ |
| Shuman ABS 710H | Shuman Plastics, Inc. | ABS | Shuman ABS |
| Karina LIGHT BLUE PVC COMP. -E600D06/958 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| POCAN® KU 2-7241 000000 | LANXESS GmbH | PBT | POCAN® |