Premi-Glas® 2206-15 CR-SX

Category:	TS, Unspecified , Thermoset, Unspecified
Manufacturer:	Premix, Inc.
Trademark:	Premi-Glas®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	MXS1UH_Premi-Glas-2206-15-CR-SX.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Premi-Glas® 2206-15 CR-SX is a fiberglass reinforced thermoset sheet molding compound for electrical, flame retardant, and HVAC applications.

Key Features and Benefits:

Non-Halogen FR technology for regulatory compliance.

Pigmentable for molded-in color; best appearance with mold texture.

UL 94-5VA flame resistance at 2.3mm minimum thickness.

Suitable for outdoor use in applications involving UV exposure and water immersion in accordance with UL746C (f1). File E42524.

This SMC product is generally intended to be compression molded in matched metal die molds, typically at 300°F (150°C) and 500 to 1000 psi (35-65 BAR) molding pressure. Strength values may be affected by the molding process. Nominal values for polymerization shrinkage (0.0015 to 0.0025 in/in) and specific gravity (1.75 to 1.85) may be customized for individual applications. Contact your Premix sales representative for specific design recommendations.

General Information
Filler / Reinforcement	Glass Fiber
Additive	Flame Retardant
Features	Flame Retardant Good Colorability Good UV Resistance Halogen Free
Uses	Electrical/Electronic Applications Outdoor Applications
UL File Number	E42524
Forms	SMC - Sheet Molding Compound
Processing Method	Compression Molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.75 to 1.85	g/cm³
Molding Shrinkage - Flow	0.15 to 0.25	%
Outdoor Suitability	f1		UL 746C

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	8960	MPa	ASTM D638
Tensile Strength	31.0	MPa	ASTM D638
Flexural Modulus	8960	MPa	ASTM D790
Flexural Strength	96.5	MPa	ASTM D790
Poisson's Ratio	0.30

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact	450	J/m	ASTM D256
Unnotched Izod Impact	590	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
CLTE
Flow	2.7E-5	cm/cm/°C
Transverse	3.6E-5	cm/cm/°C
Thermal Conductivity	0.36	W/m/K
RTI Elec	130	°C	UL 746
RTI Imp	130	°C	UL 746
RTI Str	130	°C	UL 746

Electrical	Nominal Value	Unit	Test Method
Dielectric Strength	18	kV/mm	ASTM D149
Arc Resistance	> 180	sec	ASTM D495
Comparative Tracking Index	600	V	ASTM D2303

Flammability	Nominal Value	Unit	Test Method
Flame Rating (2.31 mm)	V-0 5VA		UL 94

Resin Grade	Manufacturer	Category	Trademark
RTP 1405 B	RTP Company	PESU	RTP
Sup-tech P9000EX	Shanghai Suptech Engineering Plastics Co. Ltd.	PP, Unspecified	Sup-tech
Karina RED PVC COMP. -E 850-42/231-IS	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
Hifax CA 1168 G C1V301	LyondellBasell Industries	PP Copolymer	Hifax
Sylvin 8240-80FU White 1513	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin