APEX® RM 8002A
| Category: | PVC, Rigid , Rigid Polyvinyl Chloride |
| Manufacturer: | Teknor Apex Company |
| Trademark: | APEX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MXIIuk_APEX-RM-8002A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| APEX® RM 8002A is a Rigid Polyvinyl Chloride material. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.28 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 10 sec) | 81 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2960 | MPa | ASTM D638 |
| Tensile Strength 2(Break) | 49.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 80 | % | ASTM D638 |
| Flexural Modulus 3 | 2830 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Compression Molded) | 150 | J/m | ASTM D256 |
| Drop Impact Resistance 4(23°C) | 105 | J/cm | ASTM D4226 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed, 3.18 mm) | 69.1 | °C | ASTM D648 |
| Note Message | |
|---|---|
| 1 . | 5.1 mm/min |
| 2 . | 5.1 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | Procedure A, TUP |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 280.8 | RTP Company | Nylon 66 | RTP |
| Quadraflex™ ALE-85A | Biomerics, LLC | TPU-Polyether | Quadraflex™ |
| TPUCO® TPUE-E95 | Taiwan PU Corporation | TPU-Polyester | TPUCO® |
| Zhongfa PA66 66G30 | Yuyao Zhongfa Engineering Plastics Co. Ltd. | Nylon 66 | Zhongfa |
| Elastane™ 4720-70A | Technical Polymers, LLC | TPU-Polyester | Elastane™ |