HAIPLEN H10 T4 HT
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | HAIPLEN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MXAoa2_HAIPLEN-H10-T4-HT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene homopolymer 20% talcum filled, low flow, high stiffness and heat ageing stability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Vertical flow direction | 1.1 | % | Internal method |
| Flow direction | 1.1 | % | Internal method |
| Water Absorption (23°C, 24 hr) | 0.050 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2700 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 34.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 20 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2600 | MPa | ISO 178 |
| Flexural Stress 2 | 50.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 30 | J/m | ASTM D256 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Aging Resistance 3 | 150 | °C | Internal method |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Reinforcement Content 4(600°C) | 20 | % | ISO 3451 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 75.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 155 | °C | ISO 306/A50 |
| -- | 90.0 | °C | ISO 306/B50 |
| CLTE - Flow | 6.0E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 190 - 220 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Pre-heat Temperature: 70 to 80°CPre-heat Time: 1 hr |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 1.0 mm/min |
| 3 . | 700 hr |
| 4 . | 1 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Salflex 620TIS2 | Salflex Polymers Ltd. | PP Copolymer | Salflex |
| ARCEL® ULV (2.00 pcf) | NOVA Chemicals | PS+PE | ARCEL® |
| EZPrene 9040A | ENPLAST Americas, a Ravago Group Company | TPV | EZPrene |
| LNP™ THERMOCOMP™ EC008APQ compound | SABIC Innovative Plastics | PEI | LNP™ THERMOCOMP™ |
| ALTECH® PA6 ECO 2025/509 GF25 | ALBIS PLASTIC GmbH | Nylon 6 | ALTECH® PA6 |