TOTAL Polystyrene Impact 5331S
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polystyrene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MX39Rx_TOTAL-Polystyrene-Impact-5331S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polystyrene Impact 5331 is a high impact polystyrene for extrusion and injection molding applications. It is recommended for manufacturing of articles which require good dimensional stability. It allows good printing and retains good mechanical properties at low temperatures making it suitable for frozen packaging. Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D792 |
| Apparent Density | 0.60 | g/cm³ | ASTM D1895 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 5.0 | g/10 min | ASTM D1238, ISO 1133 |
| Spiral Flow 1 | 45.0 | cm | ASTM D3123 |
| Molding Shrinkage - Flow | 0.40 - 0.70 | % | ASTM D955 |
| Water Absorption | |||
| Balance | 0.060 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.060 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Grade R, 23°C, Injection Molding | 78 | ASTM D785 | |
| R scale, 23°C | 78 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C, Injection Molded) | 24.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break, 23°C, Injection Molded) | 40 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus (23°C, Injection Molded) | 2000 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C, injection molding | 99 | J/m | ASTM D256 |
| 23°C, injection molding | 11 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 95.0 | °C | ISO 306/A50, ASTM D1525 2 |
| CLTE - Flow | 9.1E-5 | cm/cm/°C | ASTM D696 |
| Heat Distortion | |||
| -- | 80 | °C | ISO 75-2 |
| -- | 80 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+14 | ohms | IEC 60093 |
| Dielectric Strength | 150 | kV/mm | ASTM D149 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 150 - 180 | °C | |
| Middle Temperature | 160 - 200 | °C | |
| Front Temperature | 180 - 220 | °C | |
| Nozzle Temperature | 210 - 240 | °C |
| Injection instructions |
|---|
| Zone 4 Temperature: 200 to 230°C |
| Note Message | |
|---|---|
| 1 . | Melt temperature: 220°C |
| 2 . | 速率 A (50°C/h), 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RELENE® 52GB003 | Reliance Industries Limited | HDPE | RELENE® |
| Niuk YPC6008 | Shanghai Niuk New Plastic Technology Co., Ltd. | Acetal (POM) Copolymer | Niuk |
| Aurora PVC AP2000 Series 081006 | Aurora Plastics, Inc. | PVC, Unspecified | Aurora PVC |
| Ecomass® 1850ZN66T1 | Ecomass Technologies | Nylon 6 | Ecomass® |
| MAXATEL® AC109-NAT | Pier One Polymers, Inc. | Acetal (POM) Copolymer | MAXATEL® |