DOW™ LDPE 656S
| Category: | LDPE , Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOW™ LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MWshtx_DOW-LDPE-656S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DOW™ LDPE 656S is a Low Density Polyethylene Resin material. It is available in Latin America. Typical application of DOW™ LDPE 656S: Food Contact Applications |
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.923 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.5 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic | 0.13 | ||
| vs. Itself - Static | 0.17 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Film Puncture Resistance (50 µm) | 2.00 | J/cm³ | Internal Method |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 50 µm | 10.0 | MPa | |
| TD : Yield, 50 µm | 10.0 | MPa | |
| MD : Break, 50 µm | 16.0 | MPa | |
| TD : Break, 50 µm | 15.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 50 µm | 580 | % | |
| TD : Break, 50 µm | 720 | % | |
| Dart Drop Impact (50 µm) | 89 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm | 340 | g | |
| TD : 25 µm | 330 | g |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.0 µm) | 68 | ASTM D2457 | |
| Haze (50.0 µm) | 8.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 184 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® AGV HW 35 Black E | Radici Plastics | Nylon 66 | Radilon® |
| TERRAMAC TP-4000 | UNITIKA Plastics Division | PLA | TERRAMAC |
| Vi-Chem PVC VSR87E | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| Witcom PPS 2006/351 | Witcom Engineering Plastics B.V. | PPS | Witcom PPS |
| Osterlene® HB3553 | Osterman & Company | HDPE | Osterlene® |